1) oxygen concentration cell
氧浓差电池
1.
2O9 ceramics were investigated by means of ac impedance spectroscopy, oxygen concentration cell and oxygen pump (electrochemical oxygen permeation) at 600～1000 ℃ in various at- mospher.
结果表明,氧浓差电池电动势的实测值与理论值吻合得很好,氧离子迁移数为1,表明该陶瓷样品在该温度下氧气气氛中为一纯氧离子导体;氧泵(氧的电化学透过)实验结果进一步证实了该样品在氧气气氛中为一纯氧离子导体;在氧分压p(O2)=10-5～105Pa的高氧分压气氛中,电导率与氧分压变化基本无关,表明在该氧分压范围内样品为纯离子导体,这与氧浓差电池电动势测定结果相吻合;在低氧分压为10-5～10-15Pa范围内,总电导率随氧分压降低而稍有升高,表明在该氧分压范围样品为氧离子与电子的混合导体;在600～1000℃下氧离子电导率>10-2S?cm-1,显著高于母体La2Mo2O9的氧离子电导率,1000℃时的氧离子电导率为0。
2.
In the presence of SO_2, the EMF of the oxygen concentration cell increases, but the relation between EMF and ox.
还研究了氧化锆氧浓差电池的电动势受SO_2影响的情况,有SO_2存在时,氧浓差电池的电动势增大,但电动势与氧分压的关系不再符合Nernst公式。
3.
The ion conduction properties of the ceramic sample have been studied by impedance spectra,oxygen concentration cell,oxygen pump(electrochemical oxygen permeation) techniques in the temperature range of 600～1000 ℃.
采用交流阻抗谱、氧浓差电池、氧泵等电化学方法系统地研究了该陶瓷样品在600～1000℃下的离子导电特性。
2) differential aeration cell corrosion
氧浓差电池腐蚀
4) concentration cell oxygen sensor
氧浓差电池型氧传感器
5) zirconia oxygen concentration cell
氧化锆氧浓差电池
6) steam concentration cell
水浓差电池
补充资料：盐浓差电池腐蚀
分子式：
CAS号：
性质：同一金属的不同部位所接触的介质的盐浓度不同，形成盐浓差电池而导致的腐蚀。通常，电池中与较稀溶液接触的部分，因其电极电位较负，成为电池的阳极遭到腐蚀。而与较浓溶液接触部分，由于其电极电位校正，成为电池的阴极，溶液中的金属离子可在此析出。
CAS号：
性质：同一金属的不同部位所接触的介质的盐浓度不同，形成盐浓差电池而导致的腐蚀。通常，电池中与较稀溶液接触的部分，因其电极电位较负，成为电池的阳极遭到腐蚀。而与较浓溶液接触部分，由于其电极电位校正，成为电池的阴极，溶液中的金属离子可在此析出。