1) Mace ore
Mace矿粉
1.
Mace ore,the Brazilian concentrate and the Formento ore belong to one kind of inferior iron-bearing ore from sinter performance,that is difficult to be used massively in regular production.
Mace矿粉、巴西精矿粉和Formento矿粉均属于劣质铁矿粉,在正常生产中难以大批量使用。
2) slag powder
矿粉
1.
Studies on hydration mechanism of slag powder cement;
掺矿粉水泥的水化机理研究
2.
With the development of cementitious material,slag powder is more used as high-performance admixture in cement and concrete.
随着胶凝材料技术的发展,矿粉越来越多地被应用于水泥混凝土中作高性能掺合料,不仅解决了工业废渣问题,而且实现了经济循环。
3.
The relationship between the slag powder content and the mortar strength of slagcement system (expression in activity index) was studied.
以不同掺量、不同颗粒群分布的矿粉与水泥相匹配,探讨了其与矿粉-水泥胶凝体系胶砂强度(以活性指数表示)的关系。
3) ground slag
矿粉
1.
The influence of the ground slag by Beijing-steel Plant tothe properties of resisting cracking of concrete at early age;
首钢矿粉混凝土早期抗裂性试验研究
2.
For concrete containing silica fume or ground slag , the reduction of auto-shrinkage is more effective by composite aggregate .
尤其对于含硅灰或矿粉的混凝土,复合骨料降低混凝土的自收缩效果更好。
3.
The influence of ordingary ground slag on drying shrinkage of conrete was studied in this paper.
主要研究了矿粉对混凝土干燥收缩性能的影响。
4) slag
[英][slæɡ] [美][slæg]
矿粉
1.
Influence of slag on volumetric deformation of cement motar under environment of invariable temperature and variational humidity;
恒温变湿条件下矿粉对水泥砂浆体积变形的影响
2.
The relationships of tensile-compressive-bending of concrete with micro-slag;
微矿粉高性能混凝土的拉、压、弯关系
3.
In this paper,some performances that included workability,compressive strength,elastic module,drying shrinkage and creep,were tested for hydraulic engineering concrete with and without fly ash or slag.
采用对比的方法,实验研究了粉煤灰、矿粉对水工混凝土的工作性、抗压强度、弹性模量、干缩和受压徐变的影响。
5) powder mineral
粉矿
1.
Programs were put forward according to the study on the nature of synthetical powder mineral at Huidong: + 0.
通过对会东满银沟、冶炼厂综合粉矿的性质进行研究,提出了分选综合粉矿的方案,对+0。
6) powdered ore
粉矿
1.
Energy saving effects of applied pressure filtration for gained powdered ore under the well;
采用压滤脱水提取井下粉矿的节能效果
补充资料：B矿
分子式：
CAS号：
性质：简称B矿。含有少量氧化铝、氧化铁、氧化钠、氧化镁、氧化钾等氧化物的硅酸二钙固溶体。有β、α′和α型。组成：氧化钙63.0%～63.7%，二氧化硅31.5%～33.7%，三氧化二铝1.1%～2.6%，三氧化二铁0.7%～2.2%；其余为氧化镁、氧化钠、氧化钾、二氧化钛、五氧化二磷等。二轴晶晶体折射率ng=1.735，nm=1.726，np=1.717，双折射率ng-np=0.018。硅酸盐水泥熟料中的重要矿物成分，但大多以β型存在于熟料。β型贝利特为单斜晶系，呈棱柱状或板状，在正常熟料中呈圆粒状，能使水泥石后期机械强度缓慢增长，并有抗硫酸盐侵蚀和水化热低的特点。
CAS号：
性质：简称B矿。含有少量氧化铝、氧化铁、氧化钠、氧化镁、氧化钾等氧化物的硅酸二钙固溶体。有β、α′和α型。组成：氧化钙63.0%～63.7%，二氧化硅31.5%～33.7%，三氧化二铝1.1%～2.6%，三氧化二铁0.7%～2.2%；其余为氧化镁、氧化钠、氧化钾、二氧化钛、五氧化二磷等。二轴晶晶体折射率ng=1.735，nm=1.726，np=1.717，双折射率ng-np=0.018。硅酸盐水泥熟料中的重要矿物成分，但大多以β型存在于熟料。β型贝利特为单斜晶系，呈棱柱状或板状，在正常熟料中呈圆粒状，能使水泥石后期机械强度缓慢增长，并有抗硫酸盐侵蚀和水化热低的特点。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条