1) thermal evaporation
物理热蒸发
1.
In order to control the growth of ZnO nanowires effectively,the authors have fabricated ZnO nanowires by thermal evaporation under the condition of electric field.
为了有效控制ZnO纳米线的生长,采用物理热蒸发法在外加电场的条件下制备ZnO纳米线。
2.
ZnO microrods were synthesized on Si (111) by thermal evaporation at 700℃.
利用物理热蒸发方法在光滑的(111)硅衬底上生长氧化锌微米棒,生长温度为700℃。
2) physical evaporation
物理热蒸发法
3) intercepted evaporation
截留物理蒸发
4) thermal evaporation
热蒸发
1.
Growth of ZnO nanowires by free-catalytic thermal evaporation of ZnS powder;
无催化热蒸发ZnS粉末制备半导体ZnO纳米带
2.
Aligned cone-shaped nano-ZnO structure has been synthesized by thermal evaporation of mixtures of Zn powder,C powder and ZnO powder through one step,which overcomes the disadvantage of the previous methods through two steps: preparation catalyst first and then synthesis of nano-ZnO.
将锌粉、炭粉和氧化锌粉末混合,用简单的热蒸发方法一步就合成了大量的尖锥状纳米ZnO阵列,该方法克服了其它制备方法需要先单独制备催化剂再合成ZnO的缺点而且得到产物不含杂质。
3.
Tin oxide nanoshuttle arrays were synthesized by thermal evaporation.
利用热蒸发法在硅衬底上合成了二氧化锡纳米梭阵列,并研究其场致电子发射特性。
5) thermal evaporation
热蒸发法
1.
Synthesis of ZnMgO Nanomaterials by Thermal Evaporation and Properties Characterization;
热蒸发法制备ZnMgO纳米材料及其性能表征
2.
Diamond-like carbon nanowires were synthesized by a thermal evaporation method.
采用热蒸发法制备了类金刚石碳纳米线,利用透射电子显微镜(TEM)和高分辨率透射电子显微镜(HRTEM)对样品的形貌和结构进行观察,发现该碳纳米线具有圆形实心结构,表面光滑,直径1040nm;拉曼光谱研究显示特征峰出现在1352cm-1和1586cm-1处,为典型的类金刚石结构。
3.
This paper reviews the progresses in preparation of ZnO hollow micro/nano spheres by use of simple thermal evaporation method.
文中详细地综述了由相对简单的热蒸发法合成ZnO微纳米空心球结构的制备情况和研究进展,主要包括用热蒸发法制备ZnO微纳米空心球的生产设备与过程、实验条件、产品形貌和生长机理几个方面。
6) Electrothermal vaporization
电热蒸发
1.
A method has been developed to determining directly and simultaneously the trace elements (Ca?Fe?Mn?Cu and Zn) in the food sample (maize powder) by electrothermal vaporization inductively coupled plasma atomic emission spectrometry (ETV-ICP-AES) using slurry sampling.
建立了悬浮体制样电热蒸发电感耦合等离子体原子发射光谱 (ETV -ICP -AES)法直接同时测定食品中微量元素的方法。
2.
A method was described of directly determing trace elements (La, Yb, Y Cu and Cr) in tea by electrothermal vaporization inductively coupled plasma atomic emission spectrometry (ETV-ICP-AES) using polytetrofluoroethylene (PTFE) as chemical modifier.
以聚四氟乙烯悬浮体为氟化剂 ,对悬浮体制样电热蒸发电感耦合等离子体原子发射光谱法 (ETV -ICP -AES)直接测定茶叶中的痕量元素La、Yb、Y、Cu、Cr的蒸发行为及主要影响因素进行了研究。
3.
The recent development of electrothermal vaporization/ICPAES and its application in the analysis of rare earth elements was reviewed in this paper.
评述了电热蒸发电感耦合等离子体原子发射光谱分析 (ETV -ICP -AES)联用技术的新近进展及其在痕量稀土元素检测中的应用。
补充资料：薄膜蒸发换热
薄膜蒸发换热
film evaporation heat transfer
baomo zhengfo huonre薄膜燕发换热(film evaporation heat tran-sfer)饱和液体或接近饱和温度的未饱和液体沿壁温高于饱和温度的竖管壁或竖平壁成薄膜状下流时产生的蒸发换热过程。一般下流的液体自由液面大而厚度很小。 液体沸腾换热具有很高的换热系教，其原因是:汽泡上浮引起液体对换热面强烈的冲刷运动，使液体与壁面间产生换热而急剧过热;过热的液体在汽一液两相分界面上(汽泡表面和自由液面)蒸发，一部分液体吸引其燕发潜热变成蒸汽.并使过热液体冷却变为饱和液体而再次向壁面冲刷。饱和液体对壁面的冲刷作用越强烈.液体的过热度越高，单位体积的液体所占有的汽一液两相分界面面积越大，都将导致换热系数的增高。据此，可用布膜器设计出一种人为的降膜蒸发器，将饱和液体或接近饱和温度的液体形成薄膜沿加热面流下。由于液膜很薄，液体不但具有高的过热度，而且单位体积还占有很大的汽一液两相分界面面积，因此这种降膜蒸发器具有很高的换热系数，在化工及制冷工业中已被广泛采用。 薄膜蒸发换热计算的主要目的是求出液膜厚度b与换热系数a之间的关系。20世纪50年代以来，竖管式降膜燕发器最先得到开发和推广应用。而竖板式降膜燕发器直到70年代才出现，由于它的a高、动力消耗省、不易结垢并易于除垢，近年来也得到广泛应用。无论是管式或板式，其实验研究结果都整理成无量纲膜厚度B一b(棺汁/y和液膜雷诺数R。一4厂/，之间的关系式B~。;尺扩，，以及无量纲换热系数a‘一a(y2/g汁/，与R，及普朗特数尸r一y/。之间的关系式。*一‘ZRe、介·。其中又、产、y和a分别为液体的导热率、勃度、运动猫度和热扩散率;g为重力加速度;厂为单位板宽上的液体流量;。1、nl、。2、nZ、m为实验常数，可从有关手册中查出。