1) surface forming performance
表面成形性
1.
The results show that the welding current,welding velocity and gas feed rate significantly influence the surface forming performance and mechanical properties of the welding joints.
为研究出一套适合于AM50的TIG焊接工艺,利用TIG焊接技术研究了AM50镁合金的焊接性,并调节工艺参数进行系统焊接试验,同时,对焊接接头也进行了相关的力学性能试验;试验结果表明:焊接电流、焊接速度和气体流量均对焊接接头表面成形性和力学性能产生重大影响,并得到一套完整的焊接工艺规范。
2) surface formation energy
表面形成能
3) fabric formability
面料成形性
1.
Prediction of fabric formability based on fuzzy neural network;
基于模糊神经网络的面料成形性预测
4) weld surface appearance
焊缝表面成形
1.
Sheets of wrought magnesium alloy AZ31B were welded with CO2 laser,and the influences of gas shielding condition and welding parameters on weld surface appearance were investigated.
采用3kW的CO2激光器焊接4mm厚的AZ31B变形镁合金板材,研究了气体保护方式和焊接工艺参数对焊缝表面成形的影响。
5) formation energy of surface vacancy
表面空位形成能
1.
The change of surface energy and the formation energy of surface vacancy induced by substitutional impurity were calculated.
采用嵌入原子方法的原子间相互作用势,通过分子动力学方法研究了过渡族金属Cu,Ag,Au,Ni,Pd,Pt(111)表面的相互替位掺杂对表面稳定性的影响,计算了替位掺杂体系的表面能与表面空位形成能,探讨了影响表面稳定性的因素及其变化规律。
6) surface morphology and composition
表面形貌和成分
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。