1) medium-range order
中程有序
1.
The molecular-dynamics (MD) simulation based on the tight-bind potential for a liquid Al 5Fe 2 has been carried out to invstigate the structure of medium-range order (MRO), combined with X-ray diffraction experiment.
通过对化学短程序参数α及Bhatis Thornton(BT)结构因子的分析计算 ,发现熔体中存在较强的化学序 ,并认为正是这种化学序导致了中程有序结构 (MRO)的产生 。
2.
The present thesis systematically investigated the relationships between the fragility of superheated melts and the glass-forming ability(GFA) as well as the medium-range order(MRO) in Al-based amorphous alloys.
本文以部分铝基非晶为研究对象，系统研究了过热熔体脆性与非晶形成能力及非晶中程有序结构的关系，并对非晶中的微观结构不均匀性进行了初步探究。
3.
The results of our experiments show that a distinct prepeak which characterizes medium-range order (MRO) occurs in the structure factors of each amorphous alloy.
本文以铝基非晶为研究对象,通过X射线衍射(XRD)和结构分析软件等主要手段,系统的研究了Al-Ni-Pr非晶合金的中程有序结构。
2) medium range order
中程有序
1.
0at%Fe alloy, it is found that there exists a small prepeak at 670 ℃, implying the medium range order (MRO) structure; the prepeak disappears when the temperature is up to 1400 ℃.
0at%Fe(原子百分比 )合金的结构因子曲线S(Q)上 ,温度为 6 70℃时 ,存在预峰 ,即中程有序结构 ,当温度过热到 140 0℃时 ,预峰消失 。
3) long-range order
长程有序
1.
8at% Ni at room temperature is composed of columnar B2 and granular metastable phase;the metastable phase is a disordered Al made up of Ti and Ni atoms;there is a vacancy short-range order in RS TiNi ribbon and a vacancy long-range order in RS TiNi ribbon followed by aging.
快速凝固后室温下合金的组织由柱状Ｂ２相和粒状亚稳相构成；亚稳相是由Ｔｉ、Ｎｉ两元素原子构成的无序面心立方结构；快速凝固后合金中的空位呈短程有序分布，而在４５０℃５ｍｉｎ时效后呈长程有序分布，在电子衍射图上形成１／２１００和１／４２１０额外斑点。
4) short range order
短程有序
1.
Structure of short range order in Cu and Al melt;
液态Cu和Al的短程有序结构
2.
For investigating the structure of short range order (SRO) in Cu melt, a nanocrystalline model for liquid metal was constructed.
为研究液态Cu的短程有序结构,建立了液态微观结构的纳米晶粒模型,从晶体X射线衍射学的角度出发,通过对固态Cu衍射峰的宽化计算出了液态X射线衍射强度曲线。
3.
Some Fe 2B-like and Fe 3B-like short range orders (SRO) with sizes about 1～3nm have existed in the as-quenched alloy and .
ＨＲＥＭ观察结果表明，合金淬态结构中存在有尺寸约１～３ｎｍ的类Ｆｅ２Ｂ及Ｆｅ３Ｂ短程有序区，脆化时长大至３～７ｎｍ。
5) long range order
长程有序
1.
Experimental results show that short range atomic disordering takes place during ageing in the martensite state whereas the long range order degree remians almost unchanged.
实验结果表明，淬火态ＣｕＡｌＮｉＭｎＴｉ合金在马氏体态时效过程中发生马氏体稳定化现象；在这一过程中ＤＯ３长程有序度无明显变化，但发生了原子短程无序。
2.
During parent phase aging, DO_3 atomic reordering occurs, leading to an increase in the degree of long range order.
在马氏体状态时效，ＤＯ_３长程有序度无显著变化，没发生类似在母相态的再有序化，主要是原子短程无序化。
3.
The influence of Ni-Al ordering energy from the first to the fourth layer on the atom long range order progress in Ni75Al13Cr12 alloy was investigated by microscopic phase field model.
通过微观相场方法研究了Ni75Al13Cr12合金Ni-Al第一到四层有序能对原子长程有序进程的影响。
6) short-range order
短程有序
1.
8at% Ni at room temperature is composed of columnar B2 and granular metastable phase;the metastable phase is a disordered Al made up of Ti and Ni atoms;there is a vacancy short-range order in RS TiNi ribbon and a vacancy long-range order in RS TiNi ribbon followed by aging.
快速凝固后室温下合金的组织由柱状Ｂ２相和粒状亚稳相构成；亚稳相是由Ｔｉ、Ｎｉ两元素原子构成的无序面心立方结构；快速凝固后合金中的空位呈短程有序分布，而在４５０℃５ｍｉｎ时效后呈长程有序分布，在电子衍射图上形成１／２１００和１／４２１０额外斑点。
2.
The XRD and TEM results show that short-range ordering emerges in the ribbons of Fe83Ga17 with wheel speed of 12 m·s-1, which is helpful for the magnet.
XRD和TEM分析发现,在成分为Fe83Ga17快淬薄带中,出现产生畸变的DO3结构和短程有序结构, 有助于快淬薄带磁致伸缩性能的提高。
补充资料：劳动1型中程导弹
劳动1型中程导弹是朝鲜在80年代末，于实施hwasong-6型导弹研制计划的同时，开始劳动1中程弹道导弹（国外又称为飞毛腿d）的研制计划。
劳动1采用液体推进剂，估计射程为1000～1300公里，弹头重量为800～1000公斤，发射重量15.5吨，可以打到日本的东京。在最大射程情况下，导弹的圆概率偏差为2～4公里。1993年5月朝鲜进行了迄今为止唯一的一次飞行试验，试验射程仅500公里。这并不是由于技术上的原因，而受朝鲜地理位置的限制，因为射程稍远一些就会落到别国领土或飞越别国的领空。据分析，劳动1导弹可能在1994年已完成生产型导弹的研制，最初部署的时间估计为1997年后。劳动1导弹可能采用了一组4台从飞毛腿导弹发动机改型而来的火箭发动机。该型号的研制，表明朝鲜已从早期的以单级飞毛腿导弹为基础的感制，向其第二代导弹技术研制迈出了重要一步。劳动1导弹与前苏联早期的海射型弹道导弹在重量、弹径、射程等数据方面极为相近，在设计上与前苏联在50～60年代研制和部署的ss-n-4（r-13）和ss-n-5（r-21）潜射型导弹有许多相似之处。ss-n-4采用了4台飞毛腿导弹的发动机并加长了推进剂贮箱；ss-n-5则采用了4台推力更大的发动机，其射程为1300～1600公里，弹头重680公斤，弹径1.4米。美国认为90年代初朝鲜在导弹的设计和研制上，曾得到了俄罗斯马克耶夫设计局（前苏联潜射弹道导弹设计局）的技术援助，在1992年后朝鲜劳动1导弹的研制减慢了速度，与俄罗斯停止对其提供技术援助有关。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条