1) low temperature and pressure
低温热压
1.
To extract leaching copper and iron with the technique of low temperature and pressure in complex copper concentration mineral,this paper finds out most complications which influence their rate and degree of oxidation.
通过对铜精矿进行低温热压氧化提取铜、铁的萃取工艺研究,探讨了初始酸浓度、浸出温度、浸出时间等工艺参数对铜、铁浸出率的影响。
2) low temperature and hot pressure molding
低温热模压
1.
One kind of PF resin/graphite composite was obtained by low temperature and hot pressure molding formation.
研究了低温热模压成型工艺制备酚醛树脂/石墨复合材料双极板,结果表明:酚醛树脂含量为15wt%时,复合材料的导电性能满足双极板的要求,但力学性能偏低。
3) low temperature hot-press sintering
低温热压烧结
4) Dry mixing、low temperature and hot pressure molding
干混低温热模压
6) low temperature and low pressure
低温低压
1.
Effect of using different types of zeolites,also that of operation parameters such as working temperature,method of gas inlet on the dynamic adsorption of molecule sieves pump at low temperature and low pressure is experimentally studied.
实验初步研究了分子筛吸附剂在低温低压分子筛泵动态吸附过程中的作用,同时通过变化吸附温度、进气方式等参数考察其对这一吸附过程的影响,并以LDF模型对一些现象作了解释,表明适当选择操作参数可对分子筛的这种工作能力有较大的提高。
补充资料：反应热压烧结(reactived hot pressing sintering)
分子式：
CAS号：
性质：又称反应热压烧结(reactived hot pressing sintering)或分解热压烧结(detomposition hot pressing sintering)。利用高温下粉料可能发生某种固相物理化学反应时处于较高能量的活化状态下进行热压烧结的方法。有以下几种类型：(1)相变热压烧结，如利用氧化锆在980～1100℃之间发生相变，同时进行热压，可获得高密度的细晶陶瓷；(2)分解热压烧结，如利用镁或铝的氢氧化物(或其硫酸盐)在高温下(900～1200℃)发生脱水或释气分解时，进行热压，只需加0.3～1MPa压力，保持0.5h，就可获得高密度的制品；(3)分解合成热压烧结，利用分解反应期的高度活性，在压力作用下与异类物质产生反应，然后再在压力作用下烧结成致密陶瓷，如氢氧化钡或碳酸钡分解的氧化钡与二氧化钛合成为钛酸钡等。
CAS号：
性质：又称反应热压烧结(reactived hot pressing sintering)或分解热压烧结(detomposition hot pressing sintering)。利用高温下粉料可能发生某种固相物理化学反应时处于较高能量的活化状态下进行热压烧结的方法。有以下几种类型：(1)相变热压烧结，如利用氧化锆在980～1100℃之间发生相变，同时进行热压，可获得高密度的细晶陶瓷；(2)分解热压烧结，如利用镁或铝的氢氧化物(或其硫酸盐)在高温下(900～1200℃)发生脱水或释气分解时，进行热压，只需加0.3～1MPa压力，保持0.5h，就可获得高密度的制品；(3)分解合成热压烧结，利用分解反应期的高度活性，在压力作用下与异类物质产生反应，然后再在压力作用下烧结成致密陶瓷，如氢氧化钡或碳酸钡分解的氧化钡与二氧化钛合成为钛酸钡等。