1) Cr-Mo-V New Hot Working Die Steel
Cr-Mo-V新型热作模具钢
2) HHD steel
新型高Cr热作模具钢
1.
In this paper,we weld the HHD steel by TIG, analyse properties of microstructure of the welding specimen ,and treat the welding specimen by low-temperature annealing and electropulsing which are under different parameters and roles.
本文采用TIG焊方法对新型高Cr热作模具钢进行焊接试验,主要研究低温去应力退火工艺及不同工艺参数和作用时机的脉冲电流处理工艺对补焊试件焊缝热疲劳性能的影响规律和作用机制,并采用Ansys对放电结束瞬间的温度场和应力场进行数值模拟。
3) Cr Ni Mo casting hot work die steel
Cr-Ni-Mo铸造热作模具钢
5) Cr-Mo-V steel
Cr-Mo-V钢
1.
Experimental results show that the value of threshold stress intensity factor K_ ISCC of Cr-Mo-V steel is rather low and increases slowly with the rise of tempering temperature when tempered at lower temperature and the fracture mode is mainly intergranular fracture.
当回火温度较低时,Cr-Mo-V钢的KISCC较低,且随回火温度的升高缓慢提高,断裂方式主要为沿晶断裂;当回火温度超过约873K后,KISCC显著提高,断口中穿晶断裂所占的比例明显增加,断裂方式逐渐转变为穿晶型断裂为主。
6) new Cr-Mo steel
新Cr-Mo钢
补充资料：新型特种模具钢
1. HM1热作模具钢
该钢种已纳入GB1299-85的国家标准模具钢号。它具有良好的抗热疲劳性能、抗回火稳定性能和良好的冶炼、锻造、热处理及机械加工工艺性能，是国内综合性能优良、符合我国资源条件的高强韧性热作模具新钢种。适用于高温、高负荷、急热急冷条件下的压力机锻模、轴承热锻凹模、成型滚锻模、高强度和高热强钢的精密锻造、铝和铜合金压铸模、热挤压摸具等。使用寿命可比3Cr2W8V提高1-4倍。在高温性能方面明显优于H13钢。
2．HM3热作模具钢
该钢种与HM1为同一系列产品，其高温强韧性能和热疲劳性能非常突出，特别适合于冲击载荷较大，工作温差高的模具。如辊段成型模具，有色金属压铸模具、耐热不锈钢及高强度材料锻压成型模具，轴承环套圈热锻成型凹模等，使用寿命比原用H13、3Cr2W8V和5CrNiMo都有成倍提高。
3．RM2热作模具钢
RM2钢是一种多用途基体钢，既可用于热作模具，也可用于冷作模具。该钢种已纳入GB1299-85国家标准中，具有极高的高温强度、红硬性能、热稳定性能和高温耐磨性能。特别适用于铜合金挤压模具，温锻模具和冲击载荷较小的热挤冲头模具。在切边模具、齿轮精锻模具、轴承环挤压冲头、不锈钢餐具滚轧模具的应用寿命都远高于原用H13、3Cr2W8V模具钢。
4．JDH3热作模具钢
该钢种是一种最新研制的模具材料，其性能特点是介于HM1、HM3和H13之间，即强度高于HM3，韧性高于HM1，热疲劳性能高于H13钢。主要适用于热锻模具、精锻模具、辊锻模具。