1) LiNbO_3 nanopowder
铌酸锂纳米粉
1.
LiNbO_3 nanopowders were hydrothermally synthesized at 240℃ for 12h using Li_2CO_3 and Nb_2O_5 as starting materials.
采用水热法,以Li2CO3和Nb2O5为反应物,水热反应时间为12小时,反应温度为240℃,合成了铌酸锂纳米粉体。
2) LiNbO3 powder
铌酸锂粉体
1.
The research progress of LiNbO3 powder was reviewed and several methods of producing the LiNbO3 powde, such as sol-gel method, coprecipitation method, hydrothermal method, etc were briefly summarized.
本文中分析了铌酸锂粉体的国内外研究进展,简要介绍了合成铌酸锂粉体的几种方法,如sol-gel法、沉淀法、水热法等,以及在合成结构均一、纯度高、颗粒尺寸小的铌酸锂粉体方面的研究及其应用现状。
3) nanometer lithium manganate
纳米锰酸锂
1.
Spherical nanometer lithium manganate powder was gained by detonation of unconventional slurry explosive.
首先以爆轰法合成了球形纳米锰酸锂粉体,然后对若干份实验粉体分别进行了从常温加热到300℃、400℃、500℃、600℃、700℃和800℃的烧结处理,把烧结处理好的实验样品分别在相同衍射条件下进行了X衍射分析,通过衍射曲线可以得到此纳米锰酸锂晶形变化过程。
4) Nanophase LiCoO2
纳米钴酸锂
5) LiNbO3
铌酸锂
1.
LiNbO3 ultra-fine powders were prepared via a hydrothermal method with LiOH and Nb2O5 as the starting materials.
以LiOH和Nb2O5为原料,用水热法合成了铌酸锂纳米粉体。
2.
The citrate method was adopted to prepare LiNbO3 ferroelectric film.
采用柠檬酸盐法制备铌酸锂铁电薄膜。
3.
We studied the ultraviolet-light-induced absorption coefficient change and their temperature dependence of the dark decay dynamics in the congruent LiNbO3 crystals doped with In3+ of different concentrations.
研究了不同掺杂浓度的掺铟铌酸锂晶体的紫外光致吸收和浅能级缺陷对应的热激活能。
6) Potassium lithium niobate
铌酸钾锂
1.
Potassium lithium niobate (KLN) has good photoelectric,piezoelectric and nonlinear optical properties,which has broad application in integrated optics and integrated circuits.
铌酸钾锂具有良好的光电、压电及非线性光学性能,在集成光学、集成电路等领域具有广阔的应用前景。
2.
Raman spectra of a batch of potassium lithium niobate(KLN) crystals with different compositions were investigated.
测量了一批不同组分的铌酸钾锂晶体Ram an光谱,发现晶体中位于C格位的L i离子浓度对晶体Ram an光谱产生了强烈的影响:低L i含量晶体中[NbO6]7-八面体所对应的3个Ram an特征光谱线没有发生峰分裂,在100~400 cm-1范围出现的小峰与C格位L i离子浓度相关;当晶体中L i离子浓度增加时,与ν5所对应的Ram an峰在散射几何为X(ZY)Z对应的光谱中加宽,ν2振动模式在两种散射几何中均出现分裂峰,并在100~400 cm-1范围出现小峰数量增多;当L i离子浓度接近晶体化学组分时,微扰进一步加强,5ν所对应峰分裂成3个峰,ν1和ν2振动模式发生部分分裂,在100~400 cm-1范围小峰更为突出。
3.
A series of potassium lithium niobate (KLN) crystals with large size and good homogeity for composional ions have been grown.
用电阻加热提拉法生长了一系列较大尺寸 ,组分离子均匀性较好的铌酸钾锂晶体。
补充资料：铌酸锂晶体
分子式：LiNbO3
CAS号：
性质：无色透明体。三方晶系，钛铁矿（畸变钙钛矿型）结构。熔点1253℃，密度4.648 g/cm3。莫氏硬度5，折射率n0=2.297，ne=2.208（λ=600nm），介电常数ε11=44，为铁电晶体，居里点1210℃。自发极化强度50×10-6C/cm2。以碳酸锂和五氧化二铌为原料，晶体在铂金坩埚中用提拉法生长。为一种具有压电、铁电、电光、非线性光学、热电等多性能材料，在微声技术中用于表面波、体波、换能器元件，激光技术中用于调Q开关。还可作全息记录介质材料。
CAS号：
性质：无色透明体。三方晶系，钛铁矿（畸变钙钛矿型）结构。熔点1253℃，密度4.648 g/cm3。莫氏硬度5，折射率n0=2.297，ne=2.208（λ=600nm），介电常数ε11=44，为铁电晶体，居里点1210℃。自发极化强度50×10-6C/cm2。以碳酸锂和五氧化二铌为原料，晶体在铂金坩埚中用提拉法生长。为一种具有压电、铁电、电光、非线性光学、热电等多性能材料，在微声技术中用于表面波、体波、换能器元件，激光技术中用于调Q开关。还可作全息记录介质材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。