1)  spinning
纺丝法
1.
The solution spinning,the melting spinning method craft characteristic of PLA fiber are introduced,and various working procedures craft disposition,technical measure and humidity control are discussed .
对聚乳酸纤维的溶液纺丝法、熔融纺丝法的工艺特点作了介绍。
2)  electrospinning
电纺丝法
3)  electrospinning
静电纺丝法
1.
Fabrication of MgO nanofibers by electrospinning;
静电纺丝法制备MgO纳米纤维
2.
PVA/zinc acetate composite fibers were prepared using sol-gel processing and electrospinning technique.
以聚乙烯醇作为络合剂与醋酸锌反应制得纺丝液,采用静电纺丝法制得聚乙烯醇/醋酸锌复合纤维,经煅烧后得到直径为100 nm的纯ZnO无机纳米纤维。
3.
PVP/ Mn(CH3COO)2· La(NO3)3 composite fibers were prepared by electrospinning technique with manganese acetate and PVP as starting materials.
6H2O反应制得前驱体,用静电纺丝法制备了PVP/Mn(CH3COO)2。
4)  melt spinning method
熔融纺丝法
1.
The glass-coated pure copper microwires were prepared by melt spinning method,and a study on removing the glass coat was carried out by experiment.
采用熔融纺丝法制备了玻璃包覆纯铜微丝,对微丝表面玻璃包覆层的去除进行了实验研究,评价了微丝在氢氟酸和熔融氢氧化钠中的腐蚀行为,分析了玻璃包覆纯铜微丝在强酸和强碱中的耐腐蚀性能,探讨了其腐蚀机理。
5)  Electrospinning
电场纺丝法
6)  Electrospinning method
静电纺丝法
1.
In this paper,electrospinning method was used to fabricate PCL nanofibers.
文中采用静电纺丝法制备了纳米聚己酸内酯纤维,对单根纤维进行了单向拉伸试验,研究了单根纤维在纳米尺度的基本力学性能;并通过原子力显微镜研究了纤维表面结构特征对纤维力学性能的影响。
参考词条
补充资料：复合纤维纺丝法
分子式：
CAS号：

性质： 由两种或两种以上不同性质高聚物流体，分别送入同一纺丝组件，在组件的适当部位汇合，从同一喷丝孔挤出固化成形的纺丝方法。根据复合组件结构和高聚物性质，复合纺丝法可以制成两类不同纤维：(1)采用复合纤维纺丝组件，用两种(或两种以上)性质不同，而有一定相容性的高聚物进行纺丝，在纺丝拉伸过程高聚物间不发生剥离，制成的是复合纤维；(2)采用裂片型纺丝组件，用两种(或两种以上)性质不同，而又完全不相容的高聚物进行纺丝，在纺丝拉伸或后加工过程中，不同组分高聚物间发生剥离，制成的是不同组分纤维混合的异形超细纤维。