1) Macrosegregation of boron
硼的宏观偏析
1.
Macrosegregation of boron in vacuum melting pouring ingot of GH901 alloy is determined by 3 characteristics of boron in the GH901 alloy.
GH901合金真空熔炼铸锭中硼的宏观偏析,是由硼在GH901合金中的三大特点决定的。
2.
The degree of macrosegregation of boron in vacuum melting ingot of GH2901 alloy depends on the thickness of fine crystalline zone on surface of ingot and the uniformdegree of Mo distribution on the section of the pouring ingot.
GH2901合金真空熔炼铸锭中硼的宏观偏析程度取决于铸锭表面细晶区的厚度和 Mo 在铸锭截面上分布的均匀程度。
2) macro-segregation
宏观偏析
1.
Numerical simulation of macro-segregation with equiaxed grains movement;
等轴晶移动对宏观偏析影响的数值模拟
2.
Macro-segregation Elimination in Al-9Gr Monotectic Alloy
Al-9Gr轴瓦合金控制宏观偏析的研究
3.
The effects of grain size and equiaxed grain ratio on the phosphorus macro-segregation in a weathering resistance steel have been investigated.
进行了高温模拟实验,通过改变凝固速率和添加稀土元素来改变耐候钢的凝固组织,研究了枝晶大小以及等轴晶率的不同对耐候钢中磷元素宏观偏析的影响。
3) macrosegregation
[,mækrəu,seɡrə'ɡeiʃən]
宏观偏析
1.
Study on the characteristics of central macrosegregation in moderate thickness continuous casting slabs;
中等厚度连铸板坯中心宏观偏析特性研究
2.
Numerical Simulation of Macrosegregation in Thin Slab in Continuous Casting;
薄板坯连铸凝固过程中宏观偏析的数值模拟
3.
Advance in Research on Mathematic Model of Micro- and Macrosegregation in Concasting Billet;
连铸坯微观及宏观偏析数学模型的研究进展
4) hydrogen macrosegregation
氢宏观偏析
1.
Based on Darcy s law for interdendritic flow,a mathematical model for hydrogen porosity formation in Al castings was developed,in which the hydrogen macrosegregation including hydrogen diffusion and transport in macroscopic scale was considered.
基于枝晶间流动的Darcy定律,考虑了凝固过程氢的宏观扩散与传输,建立了耦合氢宏观偏析的铝合金铸件微观孔洞形成的数学模型,并进行了实时熔炼的Al-4。
5) carbon macrosegregation
宏观碳偏析
1.
The effect of solidification condition on carbon macrosegregation of GCr15 bearing steel and the basic rule for its formation have been studied.
主要针对GCr15轴承钢凝固过程较易出现宏观碳偏析的现象,研究分析了宏观碳偏析形成的基本规律。
6) semimacrosegregation
半宏观偏析
补充资料：钢锭宏观偏析
钢锭宏观偏析
ingot macrosegregation
gangd一ng hongguan Pianxi钢锭宏观偏析(ingot maerosegregation)在钢锭中存在的限于钢锭尺寸数量级的浓度差别，又称区域偏析。通常指沿钢锭纵断面和横断面上化学成分不均匀分布情况。宏观偏析与各结晶带的形成密切相关，往往在特定区域成条带状分布。它既可用钻样分析方法进行鉴定，又可借助硫印、酸浸等低倍检验方法判明，故又称为低倍偏析。宏观偏析大小程度通常用偏析量△c=c一c。、偏析hal一c/c0或儿一导只 .、，~，‘，，一‘~，C~，一C、。_~，_100%、以及偏析差别△A一竺黔一埋翌x 100%等来量-一/’~’一F四口’一~一“C0、‘一/。、~卜王度。式中C为测定点某元素含量;C。为该元素在钢中的平均含量，常以桶样成分表示;Cma二和C、n分别为某元素在测定范围内的最高和最低含量。△c>。或Al>1称为正偏析，△C<。或A，<1则称为负偏析。宏观偏析有多种分类方法，按分布方向可分为水平偏析和垂直偏析;按偏析带形态可分为带状分析和通道偏析(如V形、倒V形偏析等);按偏析的直接成因可分为正常偏析、反常偏析、比重偏析等等。宏观偏析可使由钢锭不同部位轧制出来的钢材在机械性能和物理性能上产生很大的差异，甚至出现各向异性性，降低金属收得率，影响钢材制品的有效利用和使用寿命。如钢锭中硫的偏析能破坏金属的连续性，轧制或锻造时引起钢坯的热脆，轧制钢板时甚至引起夹层废品，严重影响钢板的冷弯性能。硫的偏析往往还是承受交变载荷的零部件引起疲劳断裂的主要根源之一。磷的偏析能使钢材制品产生冷脆性，并促进钢的回火脆性。宏观偏析将一直残留到最后产品中，危害产品的使用性能，甚至造成隐患。 (姜永林俞景录)