1) chloride ion penetration
氯离子渗透
1.
Test study on the resistance of chloride ion penetration of recycled concrete
再生混凝土抗氯离子渗透试验研究
2.
This paper analyzes the influence of SRA on the shrinkage-cracking property of HPC by designing five check-up experiments including desiccation-shrinkage,autogeous shrinkage,fiat-restraint,anti-chloride ion penetration and ultimate tensile strain.
设计了干燥收缩、自收缩、平板约束、抗氯离子渗透性以及极限拉应变等5种试验方法来检验减缩剂对高性能混凝土收缩开裂性能的影响。
3.
The chloride ion penetration in CRC with different amount of rubber particles up to 100kg/m~3 in volume,is investigated by following the ASTM C 1202-97 method.
将废旧汽车轮胎经过处理后得到的橡胶细颗粒取代部分骨料配制成橡胶集料混凝土,采用ASTM C 1202-97法对5组不同橡胶掺量的混凝土进行抗氯离子渗透性研究,结果表明,橡胶集料混凝土具有很低的氯离子渗透性,28d电量值均小于1000C,且导电量随橡胶掺量增加而减少。
2) chloride permeability
氯离子渗透
1.
The capability of chloride permeability and frost-resistant of concrete、concrete with FA and concrete with SF and FA,in 28 days as well water binder rate 0.
研究了空白混凝土、单掺FA及FA与SF复合的混凝土在水胶比为0·35,龄期为28d时在NaCl溶液中抗冻的性能和抗冻试验前后抗氯离子渗透的性能。
2.
Researches on the marine concrete show that it s difficult to achieve the low chloride permeability demand with silicate cement and mineral admixtures can improve the ability of chloride permeability.
纯硅酸盐水泥混凝土很难达到海洋高性能混凝土氯离子渗透电量小于1000C要求,矿物掺合料能够改善抗氯离子渗透能力,研究得出改善混凝土抗氯离子渗透能力依次为10%SF>60%SG>30% FA;并且通过氯离子因素耐久性经时破坏模型计算,对掺加不同矿物掺合料海洋混凝土耐久性寿命进行了预测与比较。
3.
The factors of the high-quality fly ash to the marine concrete,such as the chloride permeability、sulfate attack and shrinkage performance are studied systematicly.
通过系统研究优质粉煤灰对混凝土抗氯离子渗透、硫酸盐侵蚀、干燥收缩等性能的影响 ,根据Fick第二定律 ,在海工工程中使用适量粉煤灰可以明显改善混凝土的耐久性寿
3) Chloride ion permeability
氯离子渗透
1.
Discussion of chloride ion permeability test assessment methods in concrete;
对混凝土氯离子渗透性试验评价方法的商榷
2.
Concrete with medium or high volume ClassⅠand Class Ⅲ fly ash was designed according to the activity of fly ash,and the 7,28,90 d compressive strength,the anti-chloride ion permeability and the anticorrosion behavior of concrete were tested.
选取化学成分SiO2和Al2O3总含量相近的Ⅰ级粉煤灰和Ⅲ级粉煤灰配制中、高掺量粉煤灰混凝土,再测试其7,28,90 d抗压强度、抗氯离子渗透性能及抗钢筋锈蚀性能。
4) chloride penetration
氯离子渗透
1.
The paper use the fast test method of chloride penetration(RCM method)and nature soak method to research the capacity of aromatic and aliphatic polyurea(SPUA)coatings resist chloride penetration.
采用快速氯离子渗透实验法(RCM法)和自然扩散法两种实验方法,研究了两种混凝土保护涂层——脂肪族和芳香族喷涂聚脲(SPUA)涂层对混凝土抵抗氯离子渗透能力的影响。
5) penetration of chloride ions
氯离子渗透
1.
Influence of mineral admixture on the resistance to penetration of chloride ions into concrete;
矿物掺合料对高性能混凝土抗氯离子渗透性能的影响
2.
The test results for electric flux of 28-days and 56-days show that the influence of different superplasticizers on compressive strength is more remarkable and the application of compound mineral admixtures is a good way to improve the resistance to penetration of chloride ions of HPC.
28 d和56 d的电通量测试结果表明,减水剂品种对抗压强度的影响更为显著;复合矿物掺合料是改善高性能混凝土中氯离子渗透性的有力途径,56 d电通量均在500 C以下,其中,磨细矿渣和HK-P复掺的效果最佳。
3.
ASTM C1202 test parameters of concrete affected by penetration of chloride ions;
研究结果表明:混凝土的6h通电量、渗透深度和平均电流都随着NaCl溶液浓度的增大而增加,且不同NaCl溶液浓度下渗透深度、平均电流与6 h通电量相关性较好,可以考虑用渗透深度和平均电流作为混凝土抗氯离子渗透性评价指标。
6) chlorine ion penetration
氯离子渗透
1.
The research on the durability of concrete under the factors such as sulfate attack, chlorine ion penetration, carbonization etc, have become a hot problem of the domestic and international engineering field.
混凝土在硫酸盐侵蚀、氯离子渗透、碳化等因素影响下的耐久性研究,已成为国内外工程界研究的热点问题。
2.
The results show that the workability,freeze resistance,salt freeze resistance and resistance to chlorine ion penetration can be improved significantly by appropriate air-entrainment.
结果表明:合理的引气可显著改善混凝土的施工性能,同时混凝土的抗冻、抗盐冻性能显著提高,抗氯离子渗透性能也得到改善,并针对青岛海湾大桥的实际情况,提出了预应力引气混凝土梁的质量控制参数。
补充资料：电去离子技术和反渗透-电去离子高纯水设备
技术概况
1、采用自行研制的暗道式流道淡室隔板、国产的异相离子交换膜和离子交换树脂等材料组装的电去离子（EDI）膜堆，结合超滤、反渗透（RO）等膜分离技术成功地用于纯水、高纯水制备，结构紧凑，工艺合理，操作简便，系统设计具有创新性。
2、以RO-EDI为核心技术设计制造的1m3/h高纯水设备及小型高纯水装置工艺先进，EDI膜堆产水电阻率达到16~17MΩcm，钾、钠、锌、镍、铜、全硅、氯、硝酸根、磷酸根、硫酸根、总有机炭及细菌数等项指标达到电子级水I级标准，微粒数达到Ⅱ级标准；医药、生物技术等行业用的RO-EDI装置产水水质达到中国药典注射用水标准。
3、实验室试验及使用单位应用表明，研制的EDI膜堆可以连续稳定运行，生产纯水、高纯水。EDI膜堆污染后，可以通过清洗恢复性能。
4、研制的EDI膜堆及RO-EDI高纯水设备已经具备了产业化条件，在国内处于领先地位，并在产水水质、水耗、电耗等方面达到美国、加拿大同类品的先进水平。
5、EDI属清洁生产技术，可广泛用于电子、电力、医药、生物技术等行业生产纯水、高纯水，具有重大的社会、经济效益。
技术原理
一、基本原理
EDI是国际上九十年代才逐步成熟的纯水、高纯水生产技术、是纯水生产领域一项具有革命性的技术突破。EDI为电渗析与离子交换有机结合形成的新型膜分离技术，在外加电场的作用下，使离子交换、离子迁移、树脂电再生三个过程相伴发生，相互促进。它既保留下电渗析可连续脱盐及离子交换树脂可深度脱盐的优点，又克服了电渗析浓差极化所造成的不良影响及离子交换树脂需用酸碱再生的麻烦和造成的环境污染，可以使制水过程连续长期进行，并能获得高质量的纯水，整个过程相当于连续获得再生的混床离子交换。
二、技术关键
1、EDI淡室隔板的设计；
2、填充材料的选择；
3、EDI膜堆的组装；
4、EDI膜堆水路系统的安排；
5、EDI膜堆的操作参数。
适用范围 医药、电子、电力、生物技术和科学研究
1、采用自行研制的暗道式流道淡室隔板、国产的异相离子交换膜和离子交换树脂等材料组装的电去离子（EDI）膜堆，结合超滤、反渗透（RO）等膜分离技术成功地用于纯水、高纯水制备，结构紧凑，工艺合理，操作简便，系统设计具有创新性。
2、以RO-EDI为核心技术设计制造的1m3/h高纯水设备及小型高纯水装置工艺先进，EDI膜堆产水电阻率达到16~17MΩcm，钾、钠、锌、镍、铜、全硅、氯、硝酸根、磷酸根、硫酸根、总有机炭及细菌数等项指标达到电子级水I级标准，微粒数达到Ⅱ级标准；医药、生物技术等行业用的RO-EDI装置产水水质达到中国药典注射用水标准。
3、实验室试验及使用单位应用表明，研制的EDI膜堆可以连续稳定运行，生产纯水、高纯水。EDI膜堆污染后，可以通过清洗恢复性能。
4、研制的EDI膜堆及RO-EDI高纯水设备已经具备了产业化条件，在国内处于领先地位，并在产水水质、水耗、电耗等方面达到美国、加拿大同类品的先进水平。
5、EDI属清洁生产技术，可广泛用于电子、电力、医药、生物技术等行业生产纯水、高纯水，具有重大的社会、经济效益。
技术原理
一、基本原理
EDI是国际上九十年代才逐步成熟的纯水、高纯水生产技术、是纯水生产领域一项具有革命性的技术突破。EDI为电渗析与离子交换有机结合形成的新型膜分离技术，在外加电场的作用下，使离子交换、离子迁移、树脂电再生三个过程相伴发生，相互促进。它既保留下电渗析可连续脱盐及离子交换树脂可深度脱盐的优点，又克服了电渗析浓差极化所造成的不良影响及离子交换树脂需用酸碱再生的麻烦和造成的环境污染，可以使制水过程连续长期进行，并能获得高质量的纯水，整个过程相当于连续获得再生的混床离子交换。
二、技术关键
1、EDI淡室隔板的设计；
2、填充材料的选择；
3、EDI膜堆的组装；
4、EDI膜堆水路系统的安排；
5、EDI膜堆的操作参数。
适用范围 医药、电子、电力、生物技术和科学研究
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条