1) hydrothermal growth
水热生长
1.
Using glassy mass prepared in a platinum crucible as the raw material, colorless BSO crystals with dimensions 10×10×6 mm3 were successfully grown in 5 mol/L NaOH solution by two-step hydrothermal growth.
采用不同方法制备的培养料,进行了Bi12SiO20(BSO)晶体的水热生长实验。
2) hydrothermal method
水热生长法
1.
Bulk single crystals of Zinc Oxide(ZnO) were grown by the hydrothermal method using a pressure-resistant autoclave and a Au inner container in it for preventing impurity incorporation from the surface.
应用水热生长法,采用双温区高压反应釜、贵金属内衬,矿化剂使用KOH、NaOH和Na2CO3,生长出了毫米级六方结构的透明ZnO单晶。
2.
Bulk single crystals of Zinc Oxide(ZnO) were grown by the hydrothermal method.
本文应用水热生长法,采用双温区高压反应釜,黄金内衬(35mm×2mm),碱性溶液矿化剂,生长出了毫米级的透明氧化锌单晶,最大单晶可达2mm×3mm×6mm。
3) hydrothermal crystal growth
水热法晶体生长
4) hydrothermal crystal growth
水热晶体生长
5) crystal growth by hydrothermal method
晶体生长水热法
6) thermally grown
热生长
1.
Attention was focused on the development of bond coat and thermally grown oxide(TGO).
采用电子束物理气相沉积方法(EB PVD)在NiCoCrAlYHf粘结层上沉积YSZ热障层,研究了该热障涂层1100℃的循环氧化行为(每个循环为:1100℃保温30min、空冷5min),分析了粘结层和热生长氧化物的演化过程。
补充资料：晶体生长水热法
分子式：
CAS号：
性质： 在高温、高压水溶液中进行化学合成的一种方法。水热法不仅可以用于制备分子筛类的化合物，而且可以用来生长无机固体材料晶体。水的临界温度和压力分别为374℃和22MPa。在高温和高压下，水的离子积很大；例如在600℃和202.65MPa时，水的离子积是常温常压时的105倍。这意味着许多在通常条件下不溶于水的物质，在高温高压下可以溶于水。如果使体系产生一定的温度梯度，由于在不同温度下材料的溶解度不同，使材料晶体结晶出来。水热法生长晶体要在耐高压和高温的反应釜中进行。工业上应用水热法生长大尺寸的石英晶体。在生长晶体时，常在水中加入一定量的碱或酸，调节溶液的酸度，以调整材料在水中的溶解度。
CAS号：
性质： 在高温、高压水溶液中进行化学合成的一种方法。水热法不仅可以用于制备分子筛类的化合物，而且可以用来生长无机固体材料晶体。水的临界温度和压力分别为374℃和22MPa。在高温和高压下，水的离子积很大；例如在600℃和202.65MPa时，水的离子积是常温常压时的105倍。这意味着许多在通常条件下不溶于水的物质，在高温高压下可以溶于水。如果使体系产生一定的温度梯度，由于在不同温度下材料的溶解度不同，使材料晶体结晶出来。水热法生长晶体要在耐高压和高温的反应釜中进行。工业上应用水热法生长大尺寸的石英晶体。在生长晶体时，常在水中加入一定量的碱或酸，调节溶液的酸度，以调整材料在水中的溶解度。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。