1) γ-TiAl alloy
γ-TiAl合金
1.
Cavitation erosion of γ-TiAl alloy;
γ-TiAl合金的空蚀行为
2.
To investigate the microstructural stability,stress-strain response and fatigue fracture of a new generation γ-TiAl alloy with high Nb content under cyclic deformation,Low aycle fatigue tests under total strain controlling were carried out in the temperature range of 550℃～750℃ Deformed microstructures and fatigue fracture surfaces were observed.
为研究新一代高Nb含量γ-TiAl合金在低周疲劳过程中双态组织稳定性对应力-应变响应和疲劳断裂过程的影响,测试了Ti-47Al-5Nb合金在总应变控制条件下550℃～750℃温度范围的低周疲劳性能,并观察了循环变形后的显微组织,缺陷特征和断口形貌。
3) TiAl
合金γ-TiAl
1.
Calculation of Valence Electron Structures in Alloying γ-TiAl and Its Mechanical Properties;
合金γ-TiAl价电子结构的计算及其力学性能
4) γ-TiAl based alloy
γ-TiAl基合金
1.
Superplastic diffusion bonding of Ni based alloy/γ-TiAl based alloy;
Ni基合金/γ-TiAl基合金的超塑扩散连接
2.
To investigate the size effect of effective elastic properties for a nearly lamellar γ-TiAl based alloy,a micromechanical method was developed based on the micropolar theory.
基于微极理论细观力学方法,详细分析了近片层γ-TiAl基合金材料有效弹性性能的微结构尺度效应。
3.
With aluminum isopropoxide(Al(OC3H7)3) as precursor,an Al2O3 film was deposited on a γ-TiAl based alloy by sol-gel method.
以异丙醇铝(Al(OC3H7)3)为原料,采用溶胶-凝胶法在γ-TiAl基合金表面制备Al2O3涂层。
5) Cast γ-TiAl Alloy
铸造γ-TiAl合金
1.
Effects of Specimen Size on Microstructure of Cast γ-TiAl Alloy;
铸造γ-TiAl合金组织的尺寸效应
2.
Surface Conditions of Cast γ-TiAl Alloy;
铸造γ-TiAl合金表面状态的研究
6) high Nb-containing γ-TiAl based alloy
高铌γ-TiAl合金
补充资料：Tial
tial
tial基合金是一种新兴的金属化合物结构材料，γ-tia1合金具有许多突出特点，例如：密度低，具有高的比强度和比弹性模量，在高温时仍可以保持足够高的强度和刚度，同时它还具有良好的抗蠕变及抗氧化能力等等，这使其成为航天、航空及汽车用发动机耐热结构件极具竞争力的材料，因此，tia1合金的发展一直受到世界各国研究者的关注和重视。
tial基合金的室温延伸率通常在0.3-4％之间变化，屈服和拉伸强度则分别在250－600mpa和300－700mpa之间。早期研究的tial基合金多为铸态 。通常铸态组织为粗大树枝晶，很容易产生疏松和成分偏析，因而其脆性极高，室温延性几乎为零。
虽然tial合金有许多优点，并在技术上取得了许多重要突破，但仍有许多性能方面的问题需要解决，比如tial合金低的室温塑性及伴随而来的成形性差，对于1000℃以上使用的高温部件具有相对较低的高温强度，800℃以上的抗氧化性能不足，拉伸强度、塑性与断裂/蠕变抗力具有相反关系等，所以应用受到一定限制。