1) single-step swelling polymerization
单步溶胀聚合
1.
Uniformly sized molecularly imprinted polymeric microspheres(MIPMs) were prepared by single-step swelling polymerization using 2,4-dichloro-6,7-dimethoxyquinazoline(DCQAL) as template molecules.
以2,4-二氯-6,7-二甲氧基喹唑啉(DCQAL)为模板分子,采用单步溶胀聚合法制备了粒径均匀的分子印迹聚合物微球(M IPM s),并用静态吸附法研究了功能单体、三乙胺及水对M IPM s吸附性能的影响,考察了微球的识别性能。
2.
Naringenin molecularly imprinted polymeric microspheres (MIPMs) are prepared by single-step swelling polymerization using polystyrene as seeds.
用无皂乳液聚合法合成了微米级聚苯乙烯微粒,并以其为种球,采用单步溶胀聚合法制得了单分散柚皮素分子印迹聚合物微球(MIPMs),考察了溶胀比、水油比、溶剂种类及交联剂用量等对MIPMs形态、粒径及粒径分布的影响,并用静态吸附实验考察了MIPMs的分子识别性能。
2) one-step swelling
单步溶胀
1.
Molecularly-imprinted polymeric microspheres(MIPM) were prepared via a one-step swelling and polymerization method,with 2,4-dichloro-6,7-dimethoxyquinazoline(DCQAL) as the template molecule.
以2,4-二氯-6,7-二甲氧基喹唑啉(DCQAL)为模板分子,采用单步溶胀聚合法制得了分子印迹聚合物微球(MIPM),研究了功能单体、模板分子与功能单体的摩尔比、交联剂用量及吸附液添加剂等对MIPM识别性能的影响。
3) swelling polymerization
溶胀聚合
1.
BA was in situ grafted into PVC particles by swelling polymerization in water phase suspending system.
采用水相悬浮溶胀聚合的方法在PVC颗粒内部原位接枝丙烯酸丁酯(BA),考察了反应温度、分散剂用量对接枝反应和颗粒形态的影响,结果表明:接枝率随反应温度的升高而增大,分散剂用量为1。
4) Seed swelling and polymerization
种子溶胀聚合法
5) seed swelling polymerization
种子溶胀聚合
6) water swellable polymer
水溶胀聚合物
补充资料：抗溶胀性
分子式：
CAS号：
性质：固体浸渍于液体或暴露于蒸气中尺寸不变化的能力。当固体高聚物浸渍于溶剂，溶剂分子会渗入高聚物内部。随后，线型高聚物分子会均匀分散在溶剂中，逐渐形成完全溶解的分子分散的均相体系。对于交联的高聚物，因有交联的化学键束缚，不能再进一步使交联的分子拆散。交联度大的高聚物溶胀度小，交联度小的高聚物溶胀度大。也可以用物理的方法，比如在木材表面涂漆来阻止水分的进入材质，从而也就提高了这一构件的抗溶胀性。
CAS号：
性质：固体浸渍于液体或暴露于蒸气中尺寸不变化的能力。当固体高聚物浸渍于溶剂，溶剂分子会渗入高聚物内部。随后，线型高聚物分子会均匀分散在溶剂中，逐渐形成完全溶解的分子分散的均相体系。对于交联的高聚物，因有交联的化学键束缚，不能再进一步使交联的分子拆散。交联度大的高聚物溶胀度小，交联度小的高聚物溶胀度大。也可以用物理的方法，比如在木材表面涂漆来阻止水分的进入材质，从而也就提高了这一构件的抗溶胀性。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条