1) dihydroperoxide diisopropyl benzene
二过氧化氢二异丙苯(DHP)
2) p-diisopropylbenzene dihydroperoxide
二过氧化氢对二异丙苯
3) diisopropylbenzene hydroperoxide
过氧化氢二异丙苯
1.
Preparation of SBR 1778 with diisopropylbenzene hydroperoxide initiator;
用过氧化氢二异丙苯引发合成SBR 1778
2.
Application of 1,3-diisopropylbenzene hydroperoxide in SBR plant;
间过氧化氢二异丙苯在丁苯橡胶装置上的应用
3.
The results showed that PHP had higher catalytic activity than that of diisopropylbenzene hydroperoxide(DIP),and 54％ (mass fraction)PHP had the same initiation effect compared with that of 100％ DIP.
与过氧化氢二异丙苯（ DIP）引发聚合的对比结果表明， PHP的催化活性要比 DIP的高，同样纯度的引发剂， PHP质量分数为 DIP的 54％时二者具有相同的引发效果 ,而且对所制备胶乳性能的影响相近。
4) p-diisopropylbenzene monohydroperoxide
单过氧化氢对二异丙苯
5) Hydroperoxide,1-methyl-1-[4-(1-methylethyl)phenyl]ethyl
对过氧化氢二异丙苯
6) DCP
过氧化二异丙苯
1.
Two methods of different dynamic vulcanization processing of TPU/EVM blends in HAAKE Rheocord90 were compared in which DCP was chosen as the curing agent.
比较了通过HAAKE Rheocord90转矩流变仪用两种不同的动态硫化混炼方法对热塑性聚氨酯弹性体/乙烯-醋酸乙烯酯共聚物(TPU/EVM)共混体系性能的影响,硫化剂选用过氧化二异丙苯(DCP);探讨了密炼室转子转速和混炼温度对动态硫化共混物性能的影响。
2.
With the increasing of the concentration of DCP,gel fraction and tensile s.
随着过氧化二异丙苯用量的增加,凝胶含量和拉伸强度增加,断裂伸长率下降。
补充资料：过氧化氢二异丙苯
分子式：C12H18O2
分子量：194.24
CAS号：98-49-7
性质：淡黄色透明油状液体。熔点30℃（纯度98.8%）。受热或与酸、碱接触易分解。
制备方法：本品为异丙苯氧化制苯酚丙酮的中间副产物。在苯与丙烯反应制得的异丙苯经化液中，二异丙苯的浓度一般为11%左右。将此二异丙苯用空气直接氧化，温度为110-120℃，氧塔塔顶压力约0.3光帕，得到过氧化氢二异丙苯的氧化液，然后减压提浓至50-60%的浓度，即作为产品，相对密度为0.935-0.960（20/4℃），折光率1.4880-1.510。
用途：用作丁苯橡胶聚合用引发剂，其引发速度较过氧化氢异丙苯快30-50%，但较过氧化氢三异丙苯及过氧化氢叔丁基异丙苯为慢。也可用作其他高聚物的引发剂。本品与皮肤接触时会引起烧伤。
分子量：194.24
CAS号：98-49-7
性质：淡黄色透明油状液体。熔点30℃（纯度98.8%）。受热或与酸、碱接触易分解。
制备方法：本品为异丙苯氧化制苯酚丙酮的中间副产物。在苯与丙烯反应制得的异丙苯经化液中，二异丙苯的浓度一般为11%左右。将此二异丙苯用空气直接氧化，温度为110-120℃，氧塔塔顶压力约0.3光帕，得到过氧化氢二异丙苯的氧化液，然后减压提浓至50-60%的浓度，即作为产品，相对密度为0.935-0.960（20/4℃），折光率1.4880-1.510。
用途：用作丁苯橡胶聚合用引发剂，其引发速度较过氧化氢异丙苯快30-50%，但较过氧化氢三异丙苯及过氧化氢叔丁基异丙苯为慢。也可用作其他高聚物的引发剂。本品与皮肤接触时会引起烧伤。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。