1) intensified alkaline leaching pretreatment
碱性强化预氧化
2) alkaline aqueous chemical pre-oxidation
碱性水化学预氧化
1.
Mineral components and technological mineralogy characteristics of refractory gold ore (containing) arsentic and stibium, process of alkaline aqueous chemical pre-oxidation-cyanide leaching gold are introduced.
介绍了高砷、高锑难浸金矿石的成分、工艺矿物学特征,碱性(NaOH)水化学预氧化 氰化浸金工艺,考察了碱性水化学预氧化 氰化浸金工艺对影响金浸出的褚因素,探讨了矿石成分的改变及金难浸的原因。
3) alkaline leaching pretreatment
碱法预氧化
1.
Adopting flotation,concentrate toalkaline leaching pretreatment and cyanidation replaced the cyanidation and CIL,and only adding one set of flotation equipment,the gold recovery rate can be improved from 60% to 81%.
某金矿采用浮选—精矿加压碱法预氧化—氰化提金工艺取代原矿加压碱法预氧化—氰化提金工艺,仅增加一套浮选设备,使金回收率由原来60%提高到81%,年可多回收黄金32kg,创造效益213万元。
4) alkalinity oxidation
碱性氧化
1.
According to the different proportion, the prepared catechin monomers were reacted with the alkalinity oxidation and the acidity oxidizing reaction.
g-1的儿茶素单体,并以制备的儿茶素单体为反应原料,按照不同的比例,进行碱性氧化和酸性氧化反应,探讨儿茶素组成对茶黄素化学氧化形成的影响及作用机理。
5) alkaline peroxide impregnation
碱性过氧化氢预处理
6) basic oxide
碱性氧化物
1.
The results clearly showed that the basic oxide(Na2O) was the main component of the corrosion,Na2O in glass could decompose the mullite in brick to form α-Al2O3 and SiO2,and Na2O transformed the corundum into β- Al2O3.
结果表明，碱性氧化物（Ｎａ２Ｏ）仍然是侵蚀的主要成分，玻璃中Ｎａ２Ｏ分解砖中莫来石，形成α—Ａｌ２Ｏ３和ＳｉＯ２，Ｎａ２Ｏ把刚玉（α—Ａｌ２Ｏ３）转变成β－Ａｌ２Ｏ３，β－Ａｌ２Ｏ３在高温下由于碱的挥发，逐步溶解在玻璃中。
补充资料：磁性氧化铁环氧预涂底漆
分子式：
CAS号：
性质：是以环氧酯为主要成膜物，以磁性氧化铁为防锈颜料制成的车间预涂底漆。漆膜呈银棕色、平整无光。采用喷涂、辊涂；无空气高压喷涂施工。主要用于造船工业、铁路机车工业及钢结构件抛丸自动除锈喷涂底漆流水作业线。可与醇酸底漆、环氧底漆、硝基底膝及氯化氯丁胶底漆配套使用。
CAS号：
性质：是以环氧酯为主要成膜物，以磁性氧化铁为防锈颜料制成的车间预涂底漆。漆膜呈银棕色、平整无光。采用喷涂、辊涂；无空气高压喷涂施工。主要用于造船工业、铁路机车工业及钢结构件抛丸自动除锈喷涂底漆流水作业线。可与醇酸底漆、环氧底漆、硝基底膝及氯化氯丁胶底漆配套使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条