1) zinc borate glass
硼酸锌玻璃
2) lead zinc borate glass
硼酸铅锌玻璃
1.
The low-temperature sintering characteristics and electrical properties of ZnO-V2O5 varistors were studied through adding oxides with low melting point, which were the lead zinc borate glass frit forming materials.
研究结果表明:通过添加硼酸铅锌玻璃“形成”氧化物PbO和B2O3使其在常规电烧结炉中的烧结温度降低到了800℃,并使非线性特性明显提高,添加6wt％(PbO+B2O3)的样品经800℃ 4h烧结后,其非线性系数和漏电流密度可分别达到22。
3) zinc-borate,glass
锌硼酸盐玻璃
4) ZnO-B_2O_3-SiO_2 system glass
锌硼硅玻璃
1.
Zirconia-eontained(0%～20%(wt))ZnO-B_2O_3-SiO_2 system glass-ceramics is prepared by fusing or sintering the mixture of ZnO-B_2O_3-SiO_2 system glass and partially stabilized superfine zirconia powder.
在锌硼硅玻璃中添加0%～20%(wt)的超细部分稳定氧化锆粉体,分别采用熔融法和烧结法制备氧化锆/锌硼硅微晶玻璃。
2.
Zirconia/ZnO-B_2O_3-SiO_2 glass ceramics was prepared by sintering the mixture of zirconia(0-10 wt%)and ZnO-B_2O_3-SiO_2 system glass.
在锌硼硅玻璃中添加0%～10%(质量分数) 的部分稳定氧化锆粉体,在一定温度下烧结后制备成氧化锆/锌硼硅微晶玻璃。
5) bismuth zinc borate system glass
硼酸锌铋系统玻璃
6) borate glass
硼酸玻璃
补充资料：硼酸盐玻璃
分子式：
CAS号：
性质：以氧化硼为主要成分的玻璃。氧化硼能与许多和二氧化硅不能形成玻璃的氧化物、氟化物等形成玻璃。故可以宽广的范围内根据需要调整性能，如特高折射率、低色散、特殊色散的光学玻璃，特高热膨胀系数的电真空封接玻璃，辐射计、测量仪器玻璃，防辐射玻璃等可由硼酸盐玻璃制造。
CAS号：
性质：以氧化硼为主要成分的玻璃。氧化硼能与许多和二氧化硅不能形成玻璃的氧化物、氟化物等形成玻璃。故可以宽广的范围内根据需要调整性能，如特高折射率、低色散、特殊色散的光学玻璃，特高热膨胀系数的电真空封接玻璃，辐射计、测量仪器玻璃，防辐射玻璃等可由硼酸盐玻璃制造。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。