1) WC/Cu
WC/Cu
1.
Experimental Study on WC/Cu Composites Produced by Explosive Powder Compaction;
爆炸粉末烧结法制取WC/Cu复合材料的研究
2.
Study on Explosive Powder Compaction of WC/Cu Composites;
爆炸粉末烧结法制取WC/Cu复合材料
2) WC/Cu composite
WC弥散强化铜
1.
The influences of various cold rolling deformation ratio and annealing process on WC/Cu composite which was prepared using mechanical alloying were studied,and some abnormal changes of hardness,strength and microstructure of the materials which had appeared during high temperature annealing were also analyzed.
结果表明,冷轧变形可提高原始粉末烧结材料的致密度,材料的强度和导电率随轧制变形量的增大而增大;WC弥散强化铜材料不宜通过冷轧变形来提高其软化温度;该复合材料的退火行为在500℃下以再结晶晶粒长大为主,在600℃及其以上温度以再结晶晶粒形核为主。
3) WC/Cu composite powder
WC/Cu复合粉末
1.
Influence of high-energy ball milling time on the morphology and phase of WC/Cu composite powder was studied using XRD and SEM.
利用XRD、SEM等分析研究了高能球磨时间对WC/Cu复合粉末结构、形貌及相的影响。
4) WC/Cu composite
WCCu复合材料
5) WC/Cu composite
WC/Cu复合材料
1.
WC/Cu composite was prepared by using PM method.
用粉末冶金法制备了WC增强的WC/Cu复合材料,研究了WC含量对复合材料性能的影响,分析了复合材料的再结晶行为。
补充资料：WC-TiC-Co hard alloy
分子式：
CAS号：
性质：又称钨钛钴合金或YT合金。碳化钨、碳化钛和金属钴组成的合金。按碳化钛含量，可分为高钛(25％～40％)、中钛(10％～20％)和低钛(4％～6％)三类合金。它比碳化钨钴合金具有较高的抗氧化性，硬度和耐磨性，而抗弯强度、冲击韧性等则有所降低。主要用作切削加工钢材的工具。