1) cored wire injection process
喂线处理法
2) wire feeding process
喂线处理
1.
Basic proposes and factual effects of cored wire feeding process for cast steel melt, technical parameters and variety of alloys used in the process were introduced .
介绍了铸钢钢液喂线处理的基本目的、喂线处理的实际效果、喂线处理用合金种类及喂线处理工艺参数等 ,指出对铸钢钢液进行喂线处理可以有效降低钢中硫、氧含量 ,降低钢中非金属夹杂物总量 ,改变残留非金属夹杂物形态 ,并提高处理合金的收得率等。
3) cored-wire injection nodularizing process
喂丝球化处理法
1.
The cored-wire injection nodularizing process and its key techniques were described including: composition and preparation of cored-wire,cored-wire injection equipment and nodularizing treatment station.
列举了在两家大型企业的应用实例,指出采用喂丝球化处理必须注意的事项,探讨了喂丝球化处理法的优点,说明这种球化处理法是值得推广的球化处理新工艺,有望成为进入我国球化处理第四阶段的标志。
4) Injection feeding technology
喂线法
1.
Injection feeding technology was used to desulphurize and spheroidize ductile iron melt in industrial production .
在工业上用喂线法对铁液进行球化脱硫处理 ,通过试验确定最佳喂线速度和合适的铁液处理温度 ,并对喂线法与冲入法进行了技术、经济的比较。
5) feeding wire of sulphuration
喂线增硫法
1.
Since the unstable sulfur content and the percentage recovery of sulfur have been the ever-present problems in the course of 42CrMoS4V production,the feeding wire of sulphuration has just taken the place of FeS in ladle,the sulfur recovery of which was increased from 35% to over 75%.
生产42CrMoS4V钢时经常出现硫的回收率和硫成分不稳定问题,采用喂线增硫法替代包中加FeS后硫的收得率由35%提高到75%以上,硫成分稳定,钢的纯净度高,力学性能、超声波探伤全部满足顾客要求。
6) Feeding CaSi Wire-Adding RE Treatment
喂CaSi-加RE处理
1.
Effect of Feeding CaSi Wire-Adding RE Treatment on Inclusion and Impact Toughness of Atmosphere Corrosion Resisting Steel 09CuPTiRE;
喂CaSi-加RE处理对耐候钢09CuPTiRE夹杂物和冲击韧性的影响
补充资料：帘线表面活化处理
分子式：
CAS号：
性质：在聚酯纤维的纺丝过程牛进行表面活化处理，活化剂有封闭异氰酸酯、环氧树脂、油酸酯等。经活化处理的帘线织成帘布，采用一浴法浸渍液处理后即可得到良好的黏合效果。
CAS号：
性质：在聚酯纤维的纺丝过程牛进行表面活化处理，活化剂有封闭异氰酸酯、环氧树脂、油酸酯等。经活化处理的帘线织成帘布，采用一浴法浸渍液处理后即可得到良好的黏合效果。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条