1) perf1uoroalkyl radical
全氟烷基自由基
2) Porphyrin β-perfluoroalkylradicals
卟啉β-全氟烷基自由基
3) Alkyl perfluoroacyloxyl nitroxides
烷基-全氟酰氧基氮氧自由基
4) p-Substituted benzoyl perfluoroalkyl nitrooxides
全氟烷基对位取代苯甲酰基氮氧自由基
5) fluorocarbon radical
氟碳自由基
1.
The results showed that increasing of the bias voltage,pulse frequency,pulse width,RF power and sputtering pressure can enhance the sputtering rate of PTFE target and increase the proportion of fluorocarbon radical in plasma;especially at the peak on 25.
结果表明:增加脉冲偏压、脉冲频率、脉宽、射频功率和气压能提高Ar离子对PTFE靶的溅射能力,增加空间中氟碳自由基的数量,其中各参数对峰位位于25。
6) fluorine contained organic radicals
含氟自由基
1.
0)×105(Mw) prepared both in bulk and in solvent system polymerization using fluorine contained organic radicals as the initiator were investigated systematically.
以含氟自由基为引发剂，利用本体聚合或加入一定量的溶剂聚合并进行后处理，合成了（Ｍｗ）为（５。
补充资料：四氟乙烯-全氟烷基乙烯基醚共聚纤维
分子式：
CAS号：
性质：指共聚有少量全氟烷基乙烯基醚的可熔聚四氟乙烯纤维。一般只作单丝，密度2.2g/cm3，强度1.46cN/dtex，伸长率9％-12％，沸水收缩率12％～15％。制法是将四氟乙烯和4.4％～7％(摩尔)的共聚单体进行游离基聚合，再将树脂在340～360℃熔纺和拉伸而得。用途主要作离子交换膜的补强织物和强度要求高的耐腐蚀材料。
CAS号：
性质：指共聚有少量全氟烷基乙烯基醚的可熔聚四氟乙烯纤维。一般只作单丝，密度2.2g/cm3，强度1.46cN/dtex，伸长率9％-12％，沸水收缩率12％～15％。制法是将四氟乙烯和4.4％～7％(摩尔)的共聚单体进行游离基聚合，再将树脂在340～360℃熔纺和拉伸而得。用途主要作离子交换膜的补强织物和强度要求高的耐腐蚀材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。