1) WO3 thin film
WO3薄膜
1.
Ce-doped WO3 thin films were fabricated by DC reactive magnetron sputtering on glass substrates and annealed in dry air at 550 ℃ for 1 h.
在磁控溅射仪上用直流Ce和W共同磁控溅射方法,在载玻片上沉积Ce掺杂的WO3薄膜,以研究溅射功率对该薄膜电学性质的影响。
2.
WO3 thin film react in LiClO4 solution.
在不同氧分压条件下对WO3粉末靶进行磁控溅射,在ITO导电玻璃基底上沉积得到WO3薄膜。
3.
WO3 thin films were deposited onto glass substrates by DC magnetron sputtering technology and then it was annealed at 350~ 550 ℃.
采用直流磁控溅射法制备了WO3薄膜,并在350~550℃时对薄膜进行退火处理,研究了退火温度对薄膜结构及气敏性能的影响。
2) WO_3 thin film
WO3薄膜
1.
The electrochemistry impedance spectroscopies of ITO plane electrodes and ITO plane electrodes with WO_3 thin film immersed in 1 mol LiClO_4 propylene carbonate electrolyte have been studied by means of the surface process Faraday immittance expression and equivalent circuits.
采用表面过程法拉第阻纳表达式方法与等效电路方法,研究透明ITO平面电极及带WO3薄膜层的ITO平面电极处于1 mol LiClO4丙烯碳酸酯电解液中的电化学阻抗谱。
3) WO3 film
WO3薄膜
1.
Nano-WO3 film is the better optical gas sensor material.
WO3薄膜是良好的光学气敏传感器材料。
4) WO3-TiO2 film
WO3-TiO2薄膜
5) WO3/TiO2 thin film
WO3/TiO2薄膜
1.
In this article,photocatalytic degradation of acid red B(ARB) in aqueous solution was studied with a photocatalytic glass reactor which made of the glass beads evenly coated with transparent WO3/TiO2 thin film by the sol-gel process.
采用溶胶-凝胶法,在玻璃珠表面涂覆均匀透明的WO3/TiO2薄膜,并制成光催化反应器对水溶液中酸性红B(ARB)的光催化降解进行了研究。
6) Pt/WO3 thin film
Pt-WO3薄膜
补充资料：(beta-4)-tungstate (wo42-calcium
CAS：7790-75-2
分子式：CaO4W
中文名称：钨酸,钙白矿
英文名称：calcium tungstate；( beta-4)-tungstate (wo42-calcium ；calcium tetrahydrogen diphosphate monhydrate
分子式：CaO4W
中文名称：钨酸,钙白矿
英文名称：calcium tungstate；( beta-4)-tungstate (wo42-calcium ；calcium tetrahydrogen diphosphate monhydrate
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条