1) weld toe
焊趾
1.
Prediction of fatigue-initiation-life of surface cracks at weld toe subjected to compressive and bending loads;
压弯载荷下焊趾表面裂纹工程萌生寿命预测
2.
Statisic characteristics of stress concentration factor at weld toes;
焊趾应力集中系数的统计特性
2) welded toe
焊趾
1.
5 at the welded toe are defined as engineering crack-initiation-life.
根据前人的试验和研究成果,定义焊趾处的工程检测到的表面裂纹长度为0。
2.
Some weld defects, such as undercuts, often exist in the surface at welded toe.
接头焊趾区表面常常会存在一些焊接缺陷如咬边等,这些缺陷对接头承受动载荷的能力影响很大,疲劳裂纹往往从该部位更早地萌生。
3.
17 cruciform fillet welded specimens were tested axially under the combination of 2 stress ratios, 5 stress amplitudes and 2 post welding conditions (stress relieved and as welded) for studying the initiation of fatigue cracks from the welded toe.
１７个十字形焊接接头在两种应力比、五种应力幅值以及有、无焊接残余应力两种状态的组合下进行了轴向加载疲劳试验，以研究疲劳裂纹从焊趾“萌生”的特点。
3) weld toe defect
焊趾缺欠
4) weld toe ground
焊趾打磨
5) toe crack
焊趾裂缝
6) toe crack
焊趾裂纹