1) pack cementation
包埋共渗
1.
Al-modified silicide coatings on an Nb-silicide-based ultrahigh temperature alloy were prepared by either a two-stage pack cementation process or a co-deposition pack cementation process respectively.
分别采用两步包埋渗法和包埋共渗法在铌硅化物基合金表面制备了Al改性硅化物抗氧化涂层。
2) entrapment
包埋
1.
The physical entrapment of homogeneous transition-metal catalysts into silica sol-gel matrices is a simple procedure which makes it possible to convert a variety of soluble metal compounds into recyclable leach-proof catalysts that are more stable than their homogeneous analogues.
以正硅酸乙酯为前驱体 ,采用溶胶 凝胶技术将吡啶羧酸钴包埋进SiO2 基体中 ,于 80℃干燥 12h后得到钴含量为2 8% (Co/Si摩尔比 )的干凝胶催化剂 。
2.
In this paper, the preparation methods, advantages, disadvantage and advance of the polymer carriers for enzyme entrapment were summarized.
本文对适用于酶包埋的高分子载体材料的制备 ,优缺点以及制备载体材料的优化方法做了较为详细的叙述 ,最后对这些高分子载体材料的发展前景进行了预
3.
Chitosanase from Pseudomonas CUY8 was immobilized by cross-linking and entrapment,respectively.
采用吸附交联和包埋法对假单胞菌(Pseudomonas)CUY8产壳聚糖酶进行固定,并对游离壳聚糖酶和2种固定化酶的特性进行比较。
3) embedment
包埋
1.
Study on the embedment of salt—coagulants of instant soybean curd;
即食豆腐脑中盐类凝固剂包埋的研究
2.
Comparing all the embedment processes,the optimum of the comprehensive property of spherules as follows:the cross-link time of 24?h,the PmPD over PVA ratio of 1∶1,the PVA concentration of 8wt% with the mass loss of 15.
使用聚乙烯醇(PVA)为包埋剂,硼酸(H3BO3)为交联剂将聚间苯二胺粉末包埋成球。
3.
The study on capability of degradation of embedment of Phanerochaete chrysosporium to nitrobenzene was carried out.
实验研究了黄孢原毛平革菌的包埋固定化技术处理硝基苯废水。
4) embedding
包埋
1.
The result showed that the embedding ratio of the microencapsulated linseed oil prepared by the conditions of weight ratio of porous starch adsorbed linseed oil to 10% zein solution(1.
以多孔淀粉为载体,玉米醇溶蛋白为壁材,采用旋转锅喷雾包埋法制备粉末亚麻油。
2.
Microencapsulation of flavouring substance is an important branch of microencapsulation embedding technology.
风味物质微胶囊化是微胶囊包埋技术的一个重要分支。
3.
As sections are affected by many factors such as sampling of materials, fixation, dehydration, embedding, sectioning, mounting and staining of sections, and.
第一部分放大倍数和包埋介质对睾丸组织形态定量研究的影响 研究背景与目的: 形态定量研究中,我们通常利用组织切片,根据体视学原理测量切片上观察到的图像,由此估计组织结构的形态定量特征。
5) encapsulation
包埋
1.
The encapsulation productivity and e.
研究发现低粘度SSOS微胶囊包埋柠檬油的百分率在57。
2.
Some properties concerning sol-gel bio-encapsulation are introduced, including the basic process of sol-gel bioencapsulation, the configuration, dynamics, accessibility, activity and stability of encapsulated biomolecules.
本文主要介绍溶胶 凝胶法包埋生物分子的基本过程 ,包埋后生物分子在凝胶基质中的构象变化和运动状态 ,被分析物或底物与生物分子活性位点的接触情况以及生物分子的活性和稳定性等。
3.
The parameters of processing technology of instant Mei (Japanese apricot) were studied in this paper, problem of the juice yield and juice bitterness and astringency had been solved by the technology of enzymatic hydrolysis and encapsulation.
就青梅冲剂生产工艺条件进行了一些探讨 ,成功地应用酶解和包埋技术 ,解决了梅的出汁率问题 ,并有效地控制了梅汁苦涩味 ,达到了果汁制品理想的色、香、味 ,进而制成方便冲
6) embed
包埋
1.
Study on the influence of embedded technologies to textile fibers on the cross-sectional parameters of single hollow fibers;
纤维包埋技术对单中空纤维截面特征参数的影响
2.
Research on culture lactobacillus by the method of embed buffer salt;
包埋缓冲盐法培养乳酸菌的研究
3.
Triolein is successfully embedded into cellulose acetate (CA) by phase inversion.
采用相转化法将类脂包埋到醋酸纤维素(CA)中,制备出了具有对水中低剂量亲脂性有机污染物高效吸附去除的平板膜。
参考词条
补充资料：HF120真空离子渗碳(碳氮共渗)设备
一、设备特点：
1、加热室、过渡室、油淬室为立式结构（也可卧式）。
2、石墨碳棒加热，加热速度快，温度均匀，使用寿命。
3、脉冲偏压源，提供高稳定的强渗电源。
4、可实现气淬；油淬；真空退火；真空回火等多种工艺过程。
二、工艺特点：
1、渗碳温度可大幅度降低，实现渗碳温度与加热淬火温度一致，避免重复加热，节省能源，减小零件变形量。
2、不使用防渗剂，不渗的地方用铁板遮挡住即可，例：齿轮可先渗碳淬火再拉键槽。
3、对齿轮而言，渗碳优势明显，通过工艺控制可实现在节园部分渗层深齿根部分渗层略浅。
例如：对渗碳层深0.8mm以上。
真空离子渗碳：860℃~880℃保温2.5h+扩散0.5h淬火。
气体渗碳：930℃保温3h+扩散1h冷却，再加热至860℃淬火。
4、耗气量甚微，节能环保。
5、设备功率分别为：30/20；40/15；50/30；65/50；90/30。（电阻加热功率/辉光放电功率）。
6、工艺类型 等离子体渗碳或碳氮共渗的特点之一，是无忧机械电子在渗入的初期在工件表面就很容易建立高碳浓度，加上表面碳浓度随处理时间的延长而增加，所以必须采取渗碳加扩散的工艺（尤其对渗层较深的工件）。
7、设备示意图：
8、等离子体渗碳的原理
等离子体渗碳的原理与离子渗氮相似。工件渗碳时所需的活性碳原子或离子，不仅象常规气体渗碳一样利用热分解反应，而且还利用辉光放电时在阴极（工件）位降区中工作气体的电离而获得。以渗碳介质丙烷为例，它在等离子渗碳中的反应过程如下：
辉光放电
C3H8————————Cr+C2H6+H2
900～1000℃
辉光放电
C3H8————————Cr+CH4+H2
900～1000℃
辉光放电
C3H8————————Cr+ 2H2
900～1000℃
式中Cr 活性碳原子和离子
9、等离子渗碳的优点
⑴渗碳速度快
由于它是在真空中加热，并有高能离子的轰击，致使被处理件表面洁净与活化，再加上渗碳气体由于热分解与电离的双重作用，并在直流脉冲电场的作用下，使得工件表面附近的空间在短时间内就形成高的碳离子浓度区，从而加速了碳向工件的渗入与扩散，大大缩短渗碳时间。例如880℃，1h的离子渗碳就可获得0.6mm深的硬化层，同常规气体渗碳相比，可以缩短约50%的时间。
⑵渗层容易控制
由于工作气氛气压，放电电流密度、渗碳气体的流量及导入时间以及点燃辉光等都可以按需要预先设定并调节，因而能准确控制渗层。例如，通过调节放电电流密度值，就可以很容易控制表面碳浓度及硬化层深度。
1、加热室、过渡室、油淬室为立式结构（也可卧式）。
2、石墨碳棒加热，加热速度快，温度均匀，使用寿命。
3、脉冲偏压源，提供高稳定的强渗电源。
4、可实现气淬；油淬；真空退火；真空回火等多种工艺过程。
二、工艺特点：
1、渗碳温度可大幅度降低，实现渗碳温度与加热淬火温度一致，避免重复加热，节省能源，减小零件变形量。
2、不使用防渗剂，不渗的地方用铁板遮挡住即可，例：齿轮可先渗碳淬火再拉键槽。
3、对齿轮而言，渗碳优势明显，通过工艺控制可实现在节园部分渗层深齿根部分渗层略浅。
例如：对渗碳层深0.8mm以上。
真空离子渗碳：860℃~880℃保温2.5h+扩散0.5h淬火。
气体渗碳：930℃保温3h+扩散1h冷却，再加热至860℃淬火。
4、耗气量甚微，节能环保。
5、设备功率分别为：30/20；40/15；50/30；65/50；90/30。（电阻加热功率/辉光放电功率）。
6、工艺类型 等离子体渗碳或碳氮共渗的特点之一，是无忧机械电子在渗入的初期在工件表面就很容易建立高碳浓度，加上表面碳浓度随处理时间的延长而增加，所以必须采取渗碳加扩散的工艺（尤其对渗层较深的工件）。
7、设备示意图：
8、等离子体渗碳的原理
等离子体渗碳的原理与离子渗氮相似。工件渗碳时所需的活性碳原子或离子，不仅象常规气体渗碳一样利用热分解反应，而且还利用辉光放电时在阴极（工件）位降区中工作气体的电离而获得。以渗碳介质丙烷为例，它在等离子渗碳中的反应过程如下：
辉光放电
C3H8————————Cr+C2H6+H2
900～1000℃
辉光放电
C3H8————————Cr+CH4+H2
900～1000℃
辉光放电
C3H8————————Cr+ 2H2
900～1000℃
式中Cr 活性碳原子和离子
9、等离子渗碳的优点
⑴渗碳速度快
由于它是在真空中加热，并有高能离子的轰击，致使被处理件表面洁净与活化，再加上渗碳气体由于热分解与电离的双重作用，并在直流脉冲电场的作用下，使得工件表面附近的空间在短时间内就形成高的碳离子浓度区，从而加速了碳向工件的渗入与扩散，大大缩短渗碳时间。例如880℃，1h的离子渗碳就可获得0.6mm深的硬化层，同常规气体渗碳相比，可以缩短约50%的时间。
⑵渗层容易控制
由于工作气氛气压，放电电流密度、渗碳气体的流量及导入时间以及点燃辉光等都可以按需要预先设定并调节，因而能准确控制渗层。例如，通过调节放电电流密度值，就可以很容易控制表面碳浓度及硬化层深度。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。