1) solid solution and recrystallize treatment
固溶再结晶
1.
The results show that the 7A04 aluminum alloy obtains the optimal combination of strength and ductility in such solid solution and recrystallize treatment:470℃ 5 min+480℃ 12 min, the contradiction on dissolution of overageing phases and growth of new g.
采用力学性能检测、金相组织观察和能谱分析,试验研究了超塑预处理(SPPT)中固溶再结晶工艺对7A04铝合金组织和力学性能的影响。
2) un-recrystallization solution treatment
未再结晶固溶处理
1.
Influence of un-recrystallization solution treatment on microstructure and tensile properties of 18Ni cobalt-free maraging steel was investigated.
研究了未再结晶固溶处理对18Ni型无钴马氏体时效钢组织和拉伸性能的影响。
3) Dissolution-recrystallization
溶解-再结晶
4) solid state recrystallization
固态再结晶
5) dissolution-recrystallization reaction
溶解-再结晶反应
1.
05 are deposited on the nacre surfaces via a dissolution-recrystallization reaction.
贝壳在磷酸缓冲溶液中浸泡24h后,通过溶解-再结晶反应在其表面沉积上一层具有片状形貌的缺钙型磷灰石,其Ca/P比为(1。
6) Semi-solid Recrystallization