1) atactic polystyrene
无规聚苯乙烯
1.
In order to learn the influence of entanglements and other factors on the structural changes of atactic polystyrene, freeze-dried single-chain samples were prepared from dilute solutions of atactic poly- styrene (a-PS) in benzene at different concentrations (1×10-4 and 2×10-5 g/mL).
用冷冻升华法制备了浓度为1×10-4和2×10-5g/mL的单链无规聚苯乙烯(a-PS)。
2) Atactic Polystyrene(aPS)
无规聚苯乙烯(aPS)
3) ethylene styrene random interpolymer
乙烯/苯乙烯无规共聚物
4) Randomly branched polystyrene
无规支化聚苯乙烯
1.
Randomly branched polystyrene model compounds of known structure,which have branchedchain not only at its backbone chain but also at their branched chain are prepared for the firsttime,by coupling graft method in twice,Fifteen samplca thus obtained are characterized bymeans of the apparatus of GPC combined with a viscometer.
本文首次用两次偶合接枝的方法制备了不但在主链上有支链，而且在支链上也有支链的结构明确的无规支化聚苯乙烯模型化合物，并对所制备的１５个试样用ＣＰＣ－粘度计联用装置进行了表征。
5) poly(styrene-b-ethylene-co-butadiene-b-styrene)(SEBS)
氢化聚苯乙烯-乙烯丁烯无规共聚物-聚苯乙烯三嵌段共聚物(SEBS)
6) ethylene-styrene interpolymer (ESI)
乙烯-苯乙烯假无规共聚物(ESI)
补充资料：间规聚苯乙烯
分子式：
CAS号：
性质： 系在其大分子碳-碳主链上苯基有规则交替排列在两侧的一种结晶型苯乙烯聚合物。为一种新型透明、耐热、高电绝缘性工程塑料。熔点266℃，密度1.01g/ml，拉伸强度35MPa，弯曲模量2550MPa，热变形温度95℃(1.82MPa应力下)，介质损耗正切0.001(1mHz)。结晶速度快。常呈现多种不同晶型和晶型转变。由苯乙烯在茂金属催化剂存在下聚合制得。用作电子、电器、汽车工业用注塑件，电容器薄膜，纤维过滤元件等。
CAS号：
性质： 系在其大分子碳-碳主链上苯基有规则交替排列在两侧的一种结晶型苯乙烯聚合物。为一种新型透明、耐热、高电绝缘性工程塑料。熔点266℃，密度1.01g/ml，拉伸强度35MPa，弯曲模量2550MPa，热变形温度95℃(1.82MPa应力下)，介质损耗正切0.001(1mHz)。结晶速度快。常呈现多种不同晶型和晶型转变。由苯乙烯在茂金属催化剂存在下聚合制得。用作电子、电器、汽车工业用注塑件，电容器薄膜，纤维过滤元件等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。