1) aluminate coupling agent
铝酸酯偶联剂
1.
The paper briefly introduces the structure of silane coupling agent,titanate coupling agent and aluminate coupling agent,and mainly reviews the study and application about these three coupling agents.
对广泛应用的硅烷偶联剂、钛酸酯偶联剂和铝酸酯偶联剂的结构做了简单的介绍,主要对这三种偶联剂的研究应用情况进行了概述。
2.
The technological process of surface modification of micro-crystal muscovite by aluminate coupling agent DL-411-D and evaluation method of modification effect were studied.
经粘度和红外光谱研究证实粘度测试法是确定铝酸酯改性微晶白云母偶联剂用量的有效方法;铝酸酯偶联剂改性微晶白云母工艺简单,偶联剂用量低,不需使用稀释剂,成本低,效果好;改性后的微晶白云母在有机介质中的分散性得到显著提高,因而可大幅度提高其在高聚物中的填充量,降低复合材料的成本。
3.
The amount of polyvinyl chloride, amount of natural rubber,mass fraction of aluminate coupling agent based on amount of fly ash,and amount of fly ash were discussed.
制备了再生胶/粉煤灰路面材料,讨论了聚氯乙烯用量、天然橡胶用量、铝酸酯偶联剂质量分数(以粉煤灰用量为基准)和粉煤灰用量对其性能的影响。
2) Aluminum zirconium coupling agent
铝锆酸酯偶联剂
3) aluminum zirconium metalo organic complex coupling agent
铝-锆酸酯偶联剂
1.
This paper synthesized a new cation aluminum zirconium metalo organic complex coupling agent, and then used it in coating.
合成了一种新型的阳离子铝-锆酸酯偶联剂,并将它用于涂布纸涂料的生产,讨论了偶联剂加入前后涂料流变性、触变性、Zeta电位的变化。
4) DL-452 and NT-201
铝钛酸酯复配偶联剂
5) titanate coupling agent
钛酸酯偶联剂
1.
Application of titanate coupling agents in the inorganic fillers system;
钛酸酯偶联剂在无机填料中的应用
2.
Attapulgite was modified by titanate coupling agent NDZ311 in isopropyl alcohol by means of ultrasonic dispersion.
采用异丙醇溶解的钛酸酯偶联剂NDZ-311对凹凸棒石粘土进行超声湿法表面改性。
3.
Surface characters of anhydrite powder modified by titanate coupling agent,effects of the anhydride powder before and after modification on mechanical properties of PVC compounds and the conjoint state of PVC compounds with modified or unmodified anhydrite powder were studied.
作者研究了经钛酸酯偶联剂改性的硬石膏粉的表面性质、改性前后硬石膏粉对聚氯乙烯(PVC)复合材料的力学性能的影响以及改性前后硬石膏粉与PVC的结合情况。
6) titanate coupling reagent
钛酸酯偶联剂
1.
The surface organic modification of nano-antimicrobial and nano-antistatic agents with titanate coupling reagent,then the nano-particle is observed and investigated with the aid of TEM and contact angle dataphysics and FTIR.
选用钛酸酯偶联剂对纳米抗菌和抗静电混合粒子进行了表面修饰,并用透射电镜、接触角和红外光谱三种方法进行了表征,将经修饰的粒子与聚丙烯共混并熔融纺丝,考察了其纺丝及拉伸性能。
2.
In order to improve the diapersity of alumina polymer of high molecules and raise the biding intensity of interfaces of two phases,the surface modification of alumina by titanate coupling reagent is adopted.
为了改善氧化铝在高分子聚合物中的分散性,提高界面接合强度,采用钛酸酯偶联剂对氧化铝进行表面改性,使α-A l2O3粉体由亲水表面变成了亲油表面,提高了α-A l2O3在有机基体中的分散性和相容性,降低了体系的粘度指标,改善了加工工艺,增强了界面结合。
补充资料：铝酸酯偶联剂
外观： 白色或黄色蜡状固体
分解温度： >250℃
熔点： 70-80℃
用途
适用于多种填料，如轻、重碳酸钙、滑石粉、白碳黑、氢氧化铝、钛白粉、氧化铁红等表面活化改性处理，以及直接添加偶联剂的塑料（如：PVC、PS、ABS、PE、PEP、PU等）、橡胶、涂料、油墨、层压制品、粘结剂等复合制品。
铝酸酯偶联剂可以改善产品的加工性能和力学性能。铝酸酯在常温为固体，具有较高协同稳定性和润滑性，适用范围广、添加量小、无须稀释、使用方便、价格低廉、色浅、无毒和热稳定性好等优点。使用该种产品，能有效地改善高分子材料的加工性能及机械物理性能。填料经该种产品处理后，填料与有机物之间的接口磨擦减小，流动性变好，填料与树脂分子链之间的连接性能大大增强，使它们紧密地联系起来，提高制品的熔融指数，并能较大幅度地增加填充料的用量。
经铝酸酯偶联剂活化改性处理的各种填充料，由于表面的物化作用而生成有机长链分子层，因而由亲水性变成亲有机性，使填料表面性质发生根本性变化。对比结果，使其吸水率下降，粒径变小，吸油量减少。填料在塑料中是大分子链缠绕，提高复合材料的物理指标，改善加工性能还降低了生产成本，有明显的经济效益。