1) overburnt clinker
过烧熟料
2) clinker calcination
熟料煅烧
1.
The cement clinker calcination is a complicated industry process which is nonlinear, greatly lagged, multi-variable and strongly disturbed.
水泥熟料的煅烧是一个非线性、多变量、大滞后、强干扰的复杂工业过程，进行水泥熟料煅烧质量的预报对于实现水泥生产过程的优化控制具有重要的作用。
3) underburnt clinker
欠烧熟料
1.
Through micropolariscope study on normal clinker,overburning clinker and underburnt clinker from vertical kiln of a Shaanxi's cement factory,this paper disclosures the relationship between clinker's fine texture and technological conditions.
以陕西某水泥厂立窑熟料为研究对象,利用偏光显微镜对水泥正常熟料、过烧和欠烧熟料进行了显微结构分析,揭示了水泥熟料显微结构与烧结过程中室内温度、通风、氧分布等烧结工艺的关系。
4) clinker calcinations
熟料煅烧
1.
The Coarse-Particle-Fluidized-bed technology,which turns clinker calcinations from stack- to suspending-state,suggested by the Institute of Powder Engineering of Xi an U.
西安建筑科技大学粉体工程研究所提出了大颗粒流态化水泥熟料煅烧工艺,将水泥熟料煅烧改进为流态化煅烧,并开发出了中型热态煅烧装置。
5) sinter mixture
烧结熟料
1.
The choice of an accurate formula is necessary for gaining a high quality sinter mixture and a better techni cal and economic target.
烧结炉料配方，对混联法生产氧化铝烧结工艺过程有着十分重要作用，选择正确的配方，对获取高质量烧结熟料和较好的技术经济指标具有十分重要意义。
6) clinker sintering
熟料烧成
1.
The influence of R 2O,R 2SO 4 on clinker sintering, the mincral composition and crystal structure was studied by chemical analysis XRD and optical microscope.
采用化学分析、ＸＲＤ、光学显微镜分析等方法，较系统地研究了Ｒ２Ｏ、Ｒ２ＳＯ４对硅酸盐水泥熟料烧成、矿物组成、晶体结构的影响。
补充资料：过烧
分子式：
CAS号：
性质：制品超过烧成温度称为过烧。过烧的制品易出现变形、尺寸不符合要求、坯体或釉面有气泡等。瓷体内部液相(玻璃相)增加、晶界变宽、易出现晶体异常长大、晶粒不均匀、致密度和强度下降等。导致过烧的原因是烧成温度过高，保温时间太长。窑内温度不匀也会造成局部过烧。
CAS号：
性质：制品超过烧成温度称为过烧。过烧的制品易出现变形、尺寸不符合要求、坯体或釉面有气泡等。瓷体内部液相(玻璃相)增加、晶界变宽、易出现晶体异常长大、晶粒不均匀、致密度和强度下降等。导致过烧的原因是烧成温度过高，保温时间太长。窑内温度不匀也会造成局部过烧。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。