1) composite portland cement
复合硅酸盐水泥
1.
Study of production of high performance composite Portland cement for road with finely ground fly ash and steel slag;
利用超细粉煤灰及钢渣配制用于道路的复合硅酸盐水泥的试验研究
2.
It is considered that the porous silicon rock powder is a good natural active mixing material and is able to make mixing material portland cement or composite portland cement.
认为多孔硅质岩矿粉是一种良好的天然活性混合材料，可用于制作掺混合材料的硅酸盐水泥或复合硅酸盐水泥。
2) Compound Portland cement
复合硅酸盐水泥
1.
S or compound Portland cement with P·I clinker or P.
研究了水淬矿渣的特性，检测了不同细度、掺量的矿渣微粉与Ｐ·Ⅰ熟料或Ｐ·Ｏ配制的Ｐ·Ｓ或复合硅酸盐水泥的性质。
3) modified composite Portland cement
改性硅酸盐复合水泥
1.
To explain the mechanism of improving early strength of modified composite Portland cement, changing the content of gypsum, phosphoaluminate cement, and some additives, with orthogonal experience, and XRD, SEM, pore structure analysis etc.
通过设计正交试验探索掺磷铝酸盐水泥的改性硅酸盐复合水泥的力学性能,从石膏、磷铝酸盐水泥熟料、外加剂等因素调控,以改性后的硅酸盐复合水泥水化浆体的早期抗压强度为主要指标确定最佳方案,并与未改性的硅酸盐水泥强度作对比,并通过数据分析及XRD、SEM、孔结构分析等现代测试手段,解释改性硅酸盐复合水泥早期力学性能得以改善的机理。
4) Complex Portland cement
复合道路硅酸盐水泥
5) mixed portland cement
混合硅酸盐水泥
6) phosphoaliuminate and portland composite cement
磷铝酸盐与硅酸盐复合水泥
补充资料：复合硅酸盐水泥
分子式：
CAS号：
性质：简称复合水泥。由硅酸盐水泥熟料、两种或两种以上规定的混合材料、适量石膏磨细制成的水硬性胶凝材料。混合材料总掺加量大于15％(质量)，不超过50％(质量)。可用不超过8％的窑灰代替部分混合材料。其物理性能与普通水泥接近，但混合材料掺加量较大。其实际强度随混合材料掺加量的增加而降低。其特性与所用复掺混合材料的品种和数量有关。可通过混合材料的相互搭配并调整掺加量来改善它的性能。可消除或缓解火山灰水泥需水量和干缩性大、矿渣水泥和粉煤灰水泥早期强度低等弱点，使其各种性能达到或接近普通水泥的性能，可广泛用于工业和民用建筑工程中。