1)  active curing coagent
活性交联助剂
1.
The effects of active curing coagent N,N′-bis(furfurylidene)acetone(VP-4) on the curing characteristics,mechanical properties,crosslinking densities,hot air aging resistance as well as compression set of EPDM cured by peroxide(DCP) were studied.
研究了活性交联助剂N,N′-双亚糠基丙酮(VP-4)对过氧化物(DCP)硫化的三元乙丙橡胶(EP-DM)的硫化特性、力学性能、耐热空气老化性能、交联密度和压缩永久变形等的影响。
2)  cure activating ingredient
交联活性剂
1.
This paper studied the influence of N, N - metabenzyl bimaleimide (MPBM) resin as cure activating ingredient on crosslinking reaction of nitrile - butadiene rubber (NBR) peroxide curing system.
研究了交联活性剂N,N-间苯撑双马来酰亚胺树脂(MPBM)对丁腈橡胶(NBR)过氧化物硫化体系中硫化反应的影响。
3)  reactant crosslinking agent
活性交联剂
4)  coagent [英][kəu'eidʒənt]  [美][ko'edʒənt]
交联助剂
1.
NR latex cured with different peroxides curing systems was made, and an effect of different varieties and different addition of coagents on curing efficiency was discussed.
选用不同的过氧化物硫化体系制得硫化天然胶,在此基础上探讨了不同种类及用量的交联助剂和热处理温度对硫化效果的影响。
2.
The effects of various coagent on property of hydrogenated nitrile butadiene rubber(HNBR)blends crosslinked by peroxide,and fillers on service lifetime of the twin lip seals were studied.
研究了不同交联助剂的过氧化物硫化体系对氢化丁腈橡胶(HNBR)胶料性能的影响,以及填充补强剂对制品使用寿命的影响。
5)  assistant crosslinker
助交联剂
1.
Polypropylene (PP) was modified by peroxide initiator and assistant crosslinker.
采用过氧化物引发剂与助交联剂组合对聚丙烯(PP)进行交联改性。
6)  activated assistant
活性助剂
1.
Application of 1901 activated assistant on amino baking finish;
1901活性助剂在氨基清烘漆中的应用
补充资料:Tm-002硅烷交联剂

1. 化学名称

甲基三乙酰氧基硅烷

2. 物理性质

无色至浅黄色透明液体,较低温度下可转变为白色晶体。易吸湿,可溶于醋酸酐,遇水会交联,并产生醋酸。

3. 技术规格

外观 无色至浅黄色透明液体,或白色晶体

密度(r25)g/cm3 1.1750~ 1.1800g/cm3

含量(%) ≥95

折射率(n 25d) 1.4050±0.0005

沸点(℃) 110-112/17mmhg

熔点(℃) 40.5

cl-(%) ≤0.1

4. 用途

本品主要用作室温硫化硅橡胶的交联剂。

5. 包装与储运

塑料桶包装,每桶净重10kg、25kg、100kg、180kg。密封储存于阴凉、干燥通风处,防潮防水,远离火种、热源。

说明:补充资料仅用于学习参考,请勿用于其它任何用途。