1) Cu-Al-Y alloy
Cu-Al-Y合金
1.
Aluminizing Surface of Cu-Al-Y Alloy;
Cu-Al-Y合金表面渗铝研究
2.
The aluminizing treatment on the surface of Cu-Al-Y alloy with addition of rare earth compound CeCl3 wa.
利用稀土化合物CeCl3对Cu-Al-Y合金表面进行催渗渗铝,采有工业N2中的余氧作为内氧化介质对Cu- Al-Y合金渗铝后的试样进行内氧化,从而制备Cu-Al2O3复合材料的新方法。
3.
The aluminizing treatment on the surface of Cu-Al-Y alloy with addition of rare earth compound CeCl3 was carried out.
利用稀土化合物CeCl3对Cu-Al-Y合金表面进行催渗渗铝,采用工业N2中的余氧作为内氧化介质对Cu-Al-Y合金渗铝后的试样进行内氧化制备Al2O3/Cu复合材料的新方法,并进行了初步的试验研究与理论分析。
2) Zr-Cu-Al-Y alloy
Zr-Cu-Al-Y合金
3) Mg-Al-Cu-Y amorphous alloys
Mg-Al-Cu-Y非晶态合金
4) Cu-Y alloy
Cu-Y合金
5) Al-Y alloys
Al-Y合金
6) Cu-Al alloy
Cu-Al合金
1.
Identification of the oxide layer of Cu-Al alloy plate produced by internal oxidation;
Cu-Al合金平板试样内氧化层的测定
2.
3% com-pared with unsintered blank at the same time,and internal oxidation of Cu-Al alloy particles ocnurs.
3%;同时Cu-Al合金颗粒完成了内氧化,生成了大量粒状的Al2O3并弥散分布于铜基体,其粒径约为5~20 nm,颗粒间距约为25~60 nm。
3.
Thermodynamic requirements of internal oxidation of Cu-Al alloy were systematically analyzed, and the area chart of internal oxidation thermodynamics was drawn at the same time.
对Cu-Al合金内氧化的热力学条件进行了分析,绘制了内氧化的热力学条件区位图。
补充资料：Al-Cu cast aluminium alloy
分子式：
CAS号：
性质：以铜为主要合金元素的铸造铝合金。铜的含量范围在4％～14％。含铜9％以上的Al-Cu系合金，具有较好的铸造性能，可用于金属型铸造，并具有良好的抛光性能及电镀性能。但热处理强化效果不大，力学性能较低，主要用于装饰性零件。该系合金中具有重要应用价值的是由Al-5Cu合金基础上发展起来的高强度铸造铝合金和热强铸造铝合金。主要有Al-Cu-Si，Al-Cu-Mn，Al-Cu-Mg，Al-Cu-Ni，Al-Cu-RE等系列。Al-Cu系合金具有良好的切削加工性能和焊接性能。铸造性能较差，热裂、疏松倾向较大，需要合理的铸造工艺设计。
CAS号：
性质：以铜为主要合金元素的铸造铝合金。铜的含量范围在4％～14％。含铜9％以上的Al-Cu系合金，具有较好的铸造性能，可用于金属型铸造，并具有良好的抛光性能及电镀性能。但热处理强化效果不大，力学性能较低，主要用于装饰性零件。该系合金中具有重要应用价值的是由Al-5Cu合金基础上发展起来的高强度铸造铝合金和热强铸造铝合金。主要有Al-Cu-Si，Al-Cu-Mn，Al-Cu-Mg，Al-Cu-Ni，Al-Cu-RE等系列。Al-Cu系合金具有良好的切削加工性能和焊接性能。铸造性能较差，热裂、疏松倾向较大，需要合理的铸造工艺设计。