1) thermal fatigue resistance
热疲劳抗力
1.
This article has analyzed the reasons of the cracks on the H13 steel thicker mould produced during the quenching process, and pointed out that the proper heat treatment process is the key point to ensure the optimized obdurability and thermal fatigue resistance obtained, as well as the key point to ensure the quenching quality.
通过对H13钢加厚模在淬火过程中产生裂纹的原因进行分析,指出合适的热处理工艺是确保获得最佳的强韧性及热疲劳抗力的关键,也是确保淬火质量的关键。
2.
The effects of the heat treatment temperature and the cycle temperature upon the thermal fatigue resistance of steel 3Cr2W8V are studied.
本文研究了热处理温度和循环温度对 3Cr2 W8V钢热疲劳抗力的影响 ,探讨了热疲劳抗力与常规力学性质之间的联
2) hot fatigue resistance
热疲劳抗力
1.
Tests shown that the hotyield strength,the toughness and the hot fatigue resistance of the steel can be in creased considerably bystep quenching(austenitizing at 11 80℃)and tempering at 600℃.
试验表明，采用１１８０℃分级淬火，６００℃回火，可较大幅度地提高钢的高温屈服强度、韧性以及热疲劳抗力，从而提高压铸模的使用寿命。
3) thermal shock fatigue resistance
热震疲劳抗力
1.
The effects of TiC content on the thermal shock fatigue resistance were studied.
研究了Al2O3-TiC复合陶瓷的热震疲劳机制和TiC的添加量对其热震疲劳抗力的影响。
4) response to thermal fatigue
抗热疲劳能力
5) cold and heat fatigue strength
冷热疲劳抗力
6) Thermal fatigue resistance
抗热疲劳
1.
The best thermal fatigue resistance of GJH-2 steel-bonded carbides is obtained by heat treatment.
本文以钢结硬质合金GJH-2为研究对象,通过对不同热处理状态试样的热疲劳破坏试验,得出了提高钢结硬质合金的抗热疲劳性能的最佳热处理工艺,并借助于扫描电镜,研究了热疲劳裂纹萌生的位置、扩展途径和断口特征,为钢结硬质合金在热作模具上的应用提供了依据。
补充资料：疲劳生热试验
分子式：
CAS号：
性质：考察橡胶耐疲劳性能的一种试验。根据疲劳方式的不同可分为压缩疲劳生热、扭转疲劳生热、拉伸疲劳生热等多种形式。疲劳生热试验除要观察试样表面裂口增长情况外，对原试样还应测定其内部生热。橡胶疲劳生热性能是橡胶重要试验项目，尤其对轮胎而言，橡胶的疲劳生热是造成轮胎内部脱层、起鼓直至爆破的重要原因。
CAS号：
性质：考察橡胶耐疲劳性能的一种试验。根据疲劳方式的不同可分为压缩疲劳生热、扭转疲劳生热、拉伸疲劳生热等多种形式。疲劳生热试验除要观察试样表面裂口增长情况外，对原试样还应测定其内部生热。橡胶疲劳生热性能是橡胶重要试验项目，尤其对轮胎而言，橡胶的疲劳生热是造成轮胎内部脱层、起鼓直至爆破的重要原因。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条