1) waterborne polyurethane acrylate
水性聚氨酯丙烯酸酯
1.
A new kind of UV-curable waterborne polyurethane acrylate dispersion was synthesized based on hydroxyl-terminated polybutadiene(HTPB),poly(propylene glycol)(PPG),isophorene diisocyanate(IPDI),2hydroxy ethyl acrylate(HEA) and dimethylopropionic acid(DMPA) after neutralizing by triethylamine(TEA).
以端羟基聚丁二烯(HTPB)、聚丙二醇(PPG)、异佛尔酮二异氰酸酯(IPD I)、丙烯酸-2-羟基乙酯(HEA)、2,2-二羟甲基丙酸(DM PA)为主要原料进行聚合,经三乙胺(TEA)中和,以去离子水为溶剂乳化后,制得一种稳定的可紫外光固化的新型水性聚氨酯丙烯酸酯体系。
2) water-borne polyurethane-acrylate
水性聚氨酯/丙烯酸酯
1.
Study on the curing rate of ultraviolet curable water-borne polyurethane-acrylate;
影响水性聚氨酯/丙烯酸酯光固化速度的因素
3) waterborne polyurethane-acrylate
水性聚氨酯-丙烯酸酯
1.
Some infiuencing factors on the properties of waterborne polyurethane-acrylate emulsion have been fully studied,such as the mole ratio of-NCO/-OH,the mass fractions of DMPA and HEMA.
选用异佛尔酮二异氰酸酯(IPDI)、聚酯二元醇、二羟甲基丙酸(DMPA)、甲基丙烯酸-β-羟乙酯(HEMA)等为原料,采用阴离子自乳化法制备了紫外光(UV)固化水性聚氨酯-丙烯酸酯乳液。
2.
The effects of the photoinitiator and the mole ratio of NCO/OH on properties of UV-curable waterborne polyurethane-acrylate coatings were discussed.
选用异佛尔酮二异氰酸酯(IPD I)、聚酯二元醇、二羟甲基丙酸(DMPA)、甲基丙烯酸-β-羟乙酯(HEMA)等为原料,采用阴离子自乳化法制备了紫外光(UV)固化聚酯型水性聚氨酯-丙烯酸酯预聚体,并配以光引发剂,其涂层经紫外光固化。
4) water solublepolyurethane-acrylic ester (PUA)
水性丙烯酸改性聚氨酯
补充资料：甲基丙烯酸甲酯-丙烯酸乙酯-丙烯酸甲酯共聚物
分子式：
CAS号：
性质：甲基丙烯酸甲酯、丙烯酸乙酯、丙烯酸甲酯三元热塑性共聚物。在本体或悬浮聚合中，适量加入丙烯酸乙酯或丙烯酸甲酯或两者，可改进聚甲基丙烯酸甲酯的柔韧性和流动性。如甲基丙烯酸甲酯和少量丙烯酸酯(甲酯、乙酯)由悬浮聚合制得的模塑料，视丙烯酸酯的品种和加量不同，有的可作挤塑板用，有的可作PVC改性剂等。在溶液和乳液聚合中，甲基丙烯酸甲酯为“硬单体”，丙烯酸甲酯、丙烯酸乙酯为“软单体”，适当调节它们的比例，可制得成膜软硬度不同的液状树脂。适用于作涂料、漆料、织物和皮革处理剂等。
CAS号：
性质：甲基丙烯酸甲酯、丙烯酸乙酯、丙烯酸甲酯三元热塑性共聚物。在本体或悬浮聚合中，适量加入丙烯酸乙酯或丙烯酸甲酯或两者，可改进聚甲基丙烯酸甲酯的柔韧性和流动性。如甲基丙烯酸甲酯和少量丙烯酸酯(甲酯、乙酯)由悬浮聚合制得的模塑料，视丙烯酸酯的品种和加量不同，有的可作挤塑板用，有的可作PVC改性剂等。在溶液和乳液聚合中，甲基丙烯酸甲酯为“硬单体”，丙烯酸甲酯、丙烯酸乙酯为“软单体”，适当调节它们的比例，可制得成膜软硬度不同的液状树脂。适用于作涂料、漆料、织物和皮革处理剂等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。