1) Polyfunctional monomer
多官能单体
2) polyfunctional monomer
多官能团单体
1.
Sensitizing effects of polyfunctional monomer on radiation crosslinking of methyl vinyl silicone rubber
多官能团单体对甲基乙烯基硅橡胶的辐射交联敏化效应
2.
Silicone Rubber was crosslinked by 60Coγ-rays irradition with polyfunctional monomer-trimethylolpropane trimethacrylate(TMPTMA)as cross-linking sensitizer.
在60Coγ射线下,以多官能团单体三羟甲基丙烷三甲基丙烯酸酯(TMPTMA)作为敏化剂对硅橡胶进行辐射交联,研究了敏化剂、辐射剂量对硅橡胶的结构和力学性能的影响,并采用红外吸收光谱对辐照产物进行了表征。
3.
The polyfunctional monomers were found to prohibite the thermal degradation of sPP.
结果表明 ,多官能团单体可以明显抑制间规聚丙烯在交联过程中的 β降解 ,促进 s PP交联 。
3) multifunctional monomers
多官能度单体
1.
In this thesis, a series of multifunctional monomers were synthesized by the reaction of ethylene carbonate with amine and the Michael Addition reaction.
多官能度单体通常是指含有2个或2个以上的光活性基团的化合物,具有固化速度快、挥发性低、可以赋予固化膜交联结构等优点。
4) Polyfunctional unsaturated monomers (PFM)
多官能团不饱和单体
6) Reactive function monomer
活性官能单体
补充资料：多官能度环氧树脂复合材料
分子式：
CAS号：
性质：多官能度环氧树脂为基体的复合材料。平均每个分子中含有至少三个环氧基因，如AG-80，AGF-90即为缩水甘油胺类四官能度环氧树脂。特点是黏度低，活性大，交联密度高，对常见的各种增强纤维如玻璃纤维、碳纤维和有机纤维等具有良好的浸润性与黏附性。固化剂最好选胺类和酸酐类，尤其以芳香胺如DDM，DDS合适。它们具有较高的耐热性能，高温下(125～150℃)力学性能较好，并且有良好的耐腐蚀性、耐候性及介电性能，缺点是较脆，需加入增韧剂或其他环氧树脂混用。一般成型方法有接触成型、缠绕、层压、低压、模压成型等，可采用干、湿法预浸工艺，应用于航空航天工业中主、次结构以及耐烧蚀材料，也可用于工业中的耐热结构件。
CAS号：
性质：多官能度环氧树脂为基体的复合材料。平均每个分子中含有至少三个环氧基因，如AG-80，AGF-90即为缩水甘油胺类四官能度环氧树脂。特点是黏度低，活性大，交联密度高，对常见的各种增强纤维如玻璃纤维、碳纤维和有机纤维等具有良好的浸润性与黏附性。固化剂最好选胺类和酸酐类，尤其以芳香胺如DDM，DDS合适。它们具有较高的耐热性能，高温下(125～150℃)力学性能较好，并且有良好的耐腐蚀性、耐候性及介电性能，缺点是较脆，需加入增韧剂或其他环氧树脂混用。一般成型方法有接触成型、缠绕、层压、低压、模压成型等，可采用干、湿法预浸工艺，应用于航空航天工业中主、次结构以及耐烧蚀材料，也可用于工业中的耐热结构件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。