1) iron group sulfides
铁系硫化物
2) iron sulfides
硫铁化物
1.
This paper is aimed at introducing the authors' research of the spontaneous combustion characteristics of iron sulfides as a result of the reactions of hydrogen sulfide to the different degrees of humidity of the iron oxide black, iron oxide red and the iron hydroxide.
通过模拟储油罐中硫铁化物的生成方式,分析和研究了H2S气体在无氧条件下,与不同相对湿度的Fe2O3、Fe3O4和Fe(OH)3反应所生成的硫铁化物的自燃性。
2.
The oxidation heat of the iron sulfides is regarded as the main cause of tank fire.
油品储罐中的H2S气体在没有O2的室温条件下能与储罐内壁铁的主要腐蚀产物Fe2O3发生化学反应生成硫铁化物,硫铁化物的氧化放热是引起含硫油品储罐着火的主要原因。
3.
Self-ignition accident by sour oil tank was analyzed,and the major reason was found to be thermal oxidation of iron sulfides generated from reaction of rust with hydrogen sulfide.
通过对含硫油品储罐自燃事故的分析发现,储罐内壁铁锈与活性硫(主要为H2S)反应,生成的硫铁化物的氧化放热是导致自燃的主要原因。
3) iron sulphide
铁硫化物
1.
iron sulphides were synthesized mainly by way of gas-solid reaction ofmetallic iron or iron-nickel alloys with the mixture of H,S and H,.
铁硫化物的合成，通常是通过固-气反应来实现，本文利用电弧放电的方法。
4) Iron sulphides
硫铁化物
1.
Fe2O3,Fe(OH)3 and Fe3O4 formed by the corrosion of the inner wall of oil tank were further reacted with wet hydrogen sulphide at room temperature without the presence of oxygen to form iron sulphides,and the heat release from the oxidation of iron sulphides was the main cause of the spontaneous burning of oil tank storing sufur containing oil products.
含硫油品储罐内壁铁的腐蚀产物Fe2O3,Fe(OH)3,Fe3O4与湿H2S气体在没有O2存在的室温条件下发生化学反应生成硫铁化物,硫铁化物氧化放热是引起含硫油品储罐着火的主要原因。
5) Ironic sulfide
硫铁化合物
1.
Hydrogen sulfide,often present in sulfur-bearing crude tankers,can react with iron to form various sulfides like ferrous sulfide,ironic sulfide and ferrous disulfide,the tendency of which react with oxygen in air to form potentially explosive mixtures.
含硫原油中的活性硫(硫化氢、硫、硫醇)与罐内壁反应生成不同形式的硫铁化合物,这些化合物活性很高,与空气中的氧气反应放出大量的热使储罐内温度升高,可导致燃点低的物质发生自燃。
6) sulphide of iron
铁的硫化物
1.
Hazardous character of sulphide of iron is anaˉlyzed,it is stated that the main cause of fire accident of tank results from heat produced from self-ignition of sulphide.
分析了铁的硫化物的危害特性 ,阐述了硫化物“自燃”产生的热量是造成油罐发生火灾事故的主要原因 ,并提出了相应的防护措施 ,提高油罐日常使用的安全可靠性。
补充资料：聚对苯二甲酸丁二酯/乙烯系共聚物共混物
分子式：
CAS号：
性质： 采用各种改性的乙烯共聚物与PBT共混以增加相容性。从缺口冲击强度来看，一般比PBT提高1～2倍(添加量20％时)。所用乙烯系共聚物如LLDPE、MA-g-LLDPE、EVA等。使用MA-g-LLDPE得到的相畴变细，改性效果更好。使用机械共混法制备。
CAS号：
性质： 采用各种改性的乙烯共聚物与PBT共混以增加相容性。从缺口冲击强度来看，一般比PBT提高1～2倍(添加量20％时)。所用乙烯系共聚物如LLDPE、MA-g-LLDPE、EVA等。使用MA-g-LLDPE得到的相畴变细，改性效果更好。使用机械共混法制备。