1) glass based composites bone cement
玻璃基复合水泥
1.
The glass based composites bone cement which was made from β-tricalcium phosphate and glass based bone cement was immersed in the simulated body fluid, its microstructure and strength were investigated.
在玻璃基水泥中掺加β-磷酸三钙(β-TCP),制成玻璃基复合水泥试样。
2) glass-based bone cement
玻璃基骨水泥(GBC)
3) glass based bone cement
玻璃基骨水泥
1.
Microstructure and mechanical properties of glass based bone cement(GBC) were studied.
实验结果表明:通过浸泡于人体模拟液(simulatedbodyfluid,SBF)中,GBC内部会生成具有良好的生物活性类骨状磷灰石(hy droxyapatite,HAP),这些HAP的近似球状和柱状,端面尺寸在30～50nm,且交错生形成玻璃基骨水泥的自固化,提高内部结构的致密性,同时类骨状HAP晶体有利于增强GBC的力学性能。
2.
Microstructure and mechanical properties of glass based bone cement(GBC)were studied.
通过实验研究自固化玻璃基骨水泥(glass based bone cement,GBC)的显微结构及力学性能,讨论了显微结构对GBC 生物活性和力学性能的影响。
4) Cement Glass
水泥玻璃
5) Glass Fiber Reinforced Chloro-Oxide-Mg cement composite
玻璃纤维增强氯氧镁水泥复合材料
6) glass fiber reinforced cement composite
玻璃纤维增强水泥复合材料
补充资料：复合水泥
分子式：
CAS号：
性质：简称复合水泥。由硅酸盐水泥熟料、两种或两种以上规定的混合材料、适量石膏磨细制成的水硬性胶凝材料。混合材料总掺加量大于15％(质量)，不超过50％(质量)。可用不超过8％的窑灰代替部分混合材料。其物理性能与普通水泥接近，但混合材料掺加量较大。其实际强度随混合材料掺加量的增加而降低。其特性与所用复掺混合材料的品种和数量有关。可通过混合材料的相互搭配并调整掺加量来改善它的性能。可消除或缓解火山灰水泥需水量和干缩性大、矿渣水泥和粉煤灰水泥早期强度低等弱点，使其各种性能达到或接近普通水泥的性能，可广泛用于工业和民用建筑工程中。