1) 319 Casting aluminum alloy
319铸造铝合金
2) 319 Aluminum Alloy
319铝合金
3) casting aluminum alloy
铸造铝合金
1.
This paper discusses the molybdenum blue spectrophotometer method to determine high silicon content in casting aluminum alloys by reducing the quantity of samples and relative silicon content.
探讨了铸造铝合金中高硅的钼蓝光度分析方法,通过采取减少试样引入量、减少硅的相对含量等方式,使 方法得以适用;提出了方法的最佳分析条件,从而使分析的结果在国家标准的误差范围之内。
2.
The effects of solid solution treatment and ageing on the mechanical properties and corrosion resistance of a new corrosion resistant casting aluminum alloy were introduced.
主要介绍了不同的固溶和时效处理制度对新型耐蚀铸造铝合金力学性能、耐蚀性能的影响 ,通过对金相组织观 察和能谱分析 ,结合相图进行了讨论 ,指出 Mg2 Si相的充分固溶和均匀析出是决定 Al- 2 Mg- 3Si合金综合性能的关键因素 ,并根据材料实际应用情况最终确定了该新型耐蚀铸铝的热处理制度。
3.
Through the improvement of traditional coloring technologies, a coloring technology for casting aluminum alloy to obtain a reddish brown color film was developed.
研究了着色液中 Cu Cl2 含量、着色时间等因素对铸造铝合金 ZL 1 0 5表面着赭红色效果的影响 ,并考察了膜的耐腐蚀性能。
4) Cast Aluminum Alloy
铸造铝合金
1.
The processing technology and necessarily of surface modification for cast aluminum alloy are presented.
主要对表面合金化技术、表面敷层和电子束改性等技术应用于铸造铝合金表面改性进行总结。
2.
The melting process and heat treatment cycle of the cast aluminum alloy containing element Scandium were determined.
试验了含钪铸造铝合金的熔炼工艺和热处理工艺,分析了合金的化学成分,观察了合金的金相组织,测试了合金的力学性能。
3.
Electron beam modification process were used on the surfaces of cast aluminum alloy samples with various alloying elements.
利用电子束技术对添加不同合金化元素的铸造铝合金试样表面进行电子束改性试验研究。
5) cast aluminium alloy
铸造铝合金
1.
Development and Progress in New Marine Cast Aluminium Alloy;
船用新型铸造铝合金的研究
2.
Ni-Cr powder was mixed into paste with a organic binding agent and then painted onto the surface of cast aluminium alloy ZL108 for laser surface alloying using CO2 laser.
将Ni-Cr合金粉末用有机粘接剂调成膏状涂在铸造铝合金ZL108基体上,然后采用CO2激光进行激光表面合金化处理。
6) cast aluminium alloys
铸造铝合金
1.
It was studied that the technology conditions of microarc oxidation of ZL109 higher-silicon cast aluminium alloys and the structure,the micrograph and property of surface,the conditions of microarc oxidation ceramic coating.
研究了ZL109高硅铸造铝合金微弧氧化的工艺条件及氧化陶瓷膜的结构、表面显微形貌和性能。
2.
It was studied that the technology conditions of microarc oxidation of ZL109 higher-silicon cast aluminium alloys and the structure, the micrograph of surface, the conditions of microarc oxidation ceramic coating.
研究了ZL109高硅铸造铝合金微弧氧化的工艺条件及陶瓷氧化膜的结构、表面显微形貌和性能。
补充资料：铝-铜系铸造铝合金
分子式：
CAS号：
性质：以铜为主要合金元素的铸造铝合金。铜的含量范围在4％～14％。含铜9％以上的Al-Cu系合金，具有较好的铸造性能，可用于金属型铸造，并具有良好的抛光性能及电镀性能。但热处理强化效果不大，力学性能较低，主要用于装饰性零件。该系合金中具有重要应用价值的是由Al-5Cu合金基础上发展起来的高强度铸造铝合金和热强铸造铝合金。主要有Al-Cu-Si，Al-Cu-Mn，Al-Cu-Mg，Al-Cu-Ni，Al-Cu-RE等系列。Al-Cu系合金具有良好的切削加工性能和焊接性能。铸造性能较差，热裂、疏松倾向较大，需要合理的铸造工艺设计。