1) primary carbide
一次碳化物
1.
The results showed that adding Cr powder and graphite to Ni-based alloy powder can yield primary carbide precipitate in the surfacing layer,which obviously increases its hardness.
结果表明,在镍基合金粉中加入铬粉和石墨,堆焊层中析出了一次碳化物,可显著提高堆焊层的宏观硬度;随铬粉和石墨加入量的增加,堆焊层中一次碳化物的析出量随之增加,堆焊层的宏观硬度相应提高,最高可达62HRC,是镍基合金粉光束堆焊层的2。
2.
The results show that adding Cr powder and graphite to Ni-based alloy powder can make primary carbide precipitate in surfacing layer, which observably increase the hardness of surfacing layer.
研究结果表明,在镍基合金粉中加入铬粉和石墨,堆焊层中析出了一次碳化物,可显著提高堆焊层的宏观硬度;随铬粉和石墨加入量的增加,堆焊层中一次碳化物的析出量随之增加,堆焊层的宏观硬度相应提高,最高可达HRC62,是镍基合金粉光束堆焊层的2。
3) Secondary carbide
二次碳化物
1.
The influence of secondary carbides precipitation and transformation on hardening behavior of a 14Cr-1Mo-1.
5V高铬铸铁中二次碳化物的析出和转变对其亚临界处理硬化行为的影响。
2.
The secondary carbide precipitation behavior of K40S alloy after aging at 950℃ for 100 h was investigated.
研究了Ｋ４０Ｓ合金在９５０℃时效１００ ｈ后二次碳化物Ｍ２３Ｃ６；Ｍ６Ｃ的沉淀析出行为。
3.
The effects of varying the amount of secondary carbide on the character of matrix under three-body abrasion of wear resistant steel have been investigated.
选用三种不同碳、铬含量的耐磨钢，通过热处理获得不同数量的二次碳化物和马氏体基体。
4) secondary carbides
二次碳化物
1.
The secondary carbides have a strong influence on recrystallization rate by retarding the migration of recrystallization grain boundaries.
退火过程中析出的二次碳化物阻碍再结晶晶界的迁移,从而影响再结晶层的界面推移速率。
5) one carbon atom compound
碳一化合物
1.
With abundance resources of coal and natural gas, the synthesis of ethylene glycol from one carbon atom compounds has wide developmental field and applied foreground in China.
我国具有丰富的煤和天然气资源,以碳一化合物合成乙二醇(EG)具有广阔的发展空间和应用前景。
6) carbon chloride
一碳氯化物
补充资料：碳化硅晶须补强碳化硅陶瓷基复合材料
分子式：
CAS号：
性质：以碳化硅陶瓷为基和以碳化硅晶须为增强剂的新型陶瓷材料。通过晶须的载荷转移、拔出及裂纹偏转作用，获得比普通碳化硅更高的强度和韧性。使用温度达1400℃。是一种重要的高温结构陶瓷。用于燃气轮机叶片等高温部件和耐磨件制造。采用原位生长工艺和烧结工艺制取。
CAS号：
性质：以碳化硅陶瓷为基和以碳化硅晶须为增强剂的新型陶瓷材料。通过晶须的载荷转移、拔出及裂纹偏转作用，获得比普通碳化硅更高的强度和韧性。使用温度达1400℃。是一种重要的高温结构陶瓷。用于燃气轮机叶片等高温部件和耐磨件制造。采用原位生长工艺和烧结工艺制取。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条