1) DCPD-containing phenolic resin
双环戊二烯酚树脂
1.
Using phenol and dicyclopentadiene(DCPD) as raw materials,a DCPD-containing phenolic resin(DPR) was prepared via Friedel-Crafts alkylation and a DCPD-containing epoxy resin(DER) was prepared via epoxidation of DPR with epichlorohydrin.
以苯酚和双环戊二烯为原料,通过Friedel-Crafts反应,合成了双环戊二烯酚树脂(DPR)。
2) dicyclopentadiene resin
双环戊二烯树脂
3) DCPDCE
双环戊二烯双酚型氰酸酯树脂
1.
The curing kinetics of epoxy-dicyclopentadiene bisphenol cyanate ester(DCPDCE)resin co-poly mer system was studied by'Ozawa'and'Kissinger'methods,and the activation energy,pre-exponential factor,as well as rate constant at different temperatures and total reaction order of the co-polymer were calculated.
采用Ozawa方法和Kissinger方法研究了环氧树脂和双环戊二烯双酚型氰酸酯树脂(DCPDCE)共聚体系的固化动力学,并计算了活化能、指前因子、不同温度下的反应速率常数和共聚物的总反应级数。
4) dipentene-Phenol-epoxy resin
双戊烯-苯酚-环氧树脂
6) DCPD petroleum resin
双环戊二烯石油树脂
1.
Dicyclopentadiene(DCPD) is extracted by rectification from the byproduct C_5 fraction of ethylene cracking blends with solvent oil at a certain ratio,and then DCPD petroleum resin can be produced by free radical polymerization reaction at a certain temperature and pressure.
采用精馏分离工艺提取乙烯裂解副产物C5馏分中的双环戊二烯(DCPD),利用DCPD馏分与溶剂油按一定比例混合,在一定温度和压力的条件下通过自由基聚合反应得到双环戊二烯石油树脂,研究了反应温度、恒温搅拌时间及不同溶剂等对双环戊二烯石油树脂质量的影响,确定了双环戊二烯石油树脂热聚合温度、压力、老化时间等工艺条件。
补充资料：二氧化双环戊二烯B阶树脂模塑料
分子式：
CAS号：
性质：又称二氧化双环戊二烯B阶树脂模塑料。以二氧化双环戊二烯B阶树脂为基料配制的能采用模塑方法成型的配混料。产品性能为：弯曲强度110MPa，冲击强度5.4kJ/m2；马丁耐热240℃；体积电阻率1.3×1016Ω·cm，介电强度24.5MV/m。由二氧化双环戊二烯B阶树脂，用石英粉等作填料，再加脱模剂配混制得。可用模塑法制成耐热、耐候制品用于军工和民用方面。
CAS号：
性质：又称二氧化双环戊二烯B阶树脂模塑料。以二氧化双环戊二烯B阶树脂为基料配制的能采用模塑方法成型的配混料。产品性能为：弯曲强度110MPa，冲击强度5.4kJ/m2；马丁耐热240℃；体积电阻率1.3×1016Ω·cm，介电强度24.5MV/m。由二氧化双环戊二烯B阶树脂，用石英粉等作填料，再加脱模剂配混制得。可用模塑法制成耐热、耐候制品用于军工和民用方面。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条