1) slow strain rate tension experiment
慢应变拉伸实验
2) slow strain rate test(SSRT)
慢应变拉伸
3) SSRT
慢应变速率拉伸
1.
Stress Corrosion Cracking of polythionic acids(PSCC) of 304 SS were investigated by SSRT,SEM and metallographic analysis.
采用慢应变速率拉伸试验(SSRT)、扫描电镜断口分析以及金相显微组织分析等方法对304不锈钢连多硫酸应力腐蚀开裂(PSCC)行为进行了研究。
2.
The stress corrosion behavior of 304 stainless steel in the solution saturated by H2S and the standard solution of NACE was studied with electrochemical test and slow strain rate tension(SSRT) test.
用电化学测试及慢应变速率拉伸试验(SSRT)方法对304不锈钢在饱和H2S溶液和NACE标准溶液中的应力腐蚀行为进行研究。
3.
Stress Corrosion cracking of acids media(PSCC) of duplex stainles steel and ferritic stainless steel were investigated by SSRT,SEM and metallographic analysis and evaluate stress corrosion cracking sensitivity of ferritic stainless steel and duplex stainless steel in acids media.
采用慢应变速率拉伸试验(SSRT)、扫描电镜(SEM)断口分析以及金相显微组织分析等方法对TP405铁素体不锈钢及2205双相不锈钢在酸性介质中应力腐蚀开裂(PSCC)行为进行了研究。
4) slow strain rate tension
慢应变速率拉伸
1.
The stress corrosion cracking (SCC) behaviors of X80 pipeline steel in near-neutral pH solutions were studied using electrochemical potentiodynamic scanning,slow strain rate tension(SSRT) and scanning electron microscopy.
采用电化学动电位扫描技术、慢应变速率拉伸(SSRT)试验和扫描电镜观察研究了X80管线钢及焊接接头在NS4溶液中的应力腐蚀行为。
2.
5% NaCl solution was investigated by using slow strain rate tension,scanning electron microscope and transmission electron microscope.
通过慢应变速率拉伸测试、扫描电镜及透射电镜分析等研究了2519铝合金在T6、T8热处理状态下,在空气和3。
3.
The interaction between mechanics and electrochemistry during the stress corrosion cracking (SCC) of 7075 aluminum alloy was studied using slow strain rate tension (SSRT) technique.
用慢应变速率拉伸(SSRT)技术研究了7075铝合金在应力腐蚀过程中的力学与电化学交互作用。
5) slow strain rate test
慢应变速率拉伸
1.
The behavior of solid copper-induced embrittlement(SCIE) of TC11 titanium alloy was investigated using slow strain rate tests(SSRT) and constant load tensile tests(DLTT) at different temperatures.
分别采用慢应变速率拉伸、恒载荷拉伸加载方法研究了TC11钛合金在不同温度下的Cu脆行为,Cu与钛合金试样表面的接触分别采用离子束增强沉积和机械压合法实现。
2.
The behaviors of stress corrosion cracking (SCC) of 7075 aluminum alloys with different heat treatments had been tested at various polarization potentials with slow strain rate test (SSRT) method.
为了探讨极化对铝合金SCC敏感性的影响,采用慢应变速率拉伸技术研究了不同恒电位极化条件下7075T6、7075T7351、7075RRA铝合金的应力腐蚀行为。
6) slow strain rate tensile
慢应变率拉伸