1) MBS latex
MBS胶乳
1.
Research on pilotscale synthesis of MBS resin (Ⅱ) Synthesis of MBS latex;
MBS树脂合成技术的中试研究 (Ⅱ)MBS胶乳的合成
2.
Research on pilotscale synthesis of MBS resin (Ⅲ) Coagulation of MBS latex;
MBS树脂合成技术的中试研究 (Ⅲ)MBS胶乳的凝聚
3.
A new method of MBS latex coagulation by SO2 as a coagulant was proposed.
提出了用二氧化硫凝聚MBS胶乳的新方法,研究了各种因素对凝聚时间、颗粒粒径分布和粉体堆积密度的影响,确定了最佳工艺条件:MBS胶乳的质量浓度为80～120g/L,凝聚温度50～60℃,搅拌速度200r/min,二氧化硫体积流量25L/min。
2) latex
[英]['leɪteks] [美]['letɛks]
胶乳
1.
Experiment of salt-resisting performance of polyvinyl alcohol latex oil-well cement;
聚乙烯醇胶乳油井水泥抗盐性能实验
2.
Synthesis of large particle polybutyl acrylate latex;
大粒径聚丙烯酸丁酯胶乳的制备
3.
Improvement of latex on mechanical deformation capability of cement sheath under triaxial loading condition;
胶乳对水泥石三轴力学形变能力的作用
3) emulsion
[英][ɪ'mʌlʃn] [美][ɪ'mʌlʃən]
乳胶
1.
The initiator is summarized in grafting copolymerization preparation emulsion with using starch and ethenyl monomer , each kind of initiator mechanism is commented, influence of the initiator selecting to the emulsion performance is elaborated.
总结了淀粉与乙烯基单体接枝共聚制备乳胶常用的引发剂,对各类引发剂的机理作了评述,讨论引发剂的选用对乳胶性能的影响。
2.
The process of manufacturing emulsion products and its capacity indexes have been analyzed in this paper.
本文分析了乳胶制品的生产过程，并对工序能力指数进行了分析，从而推断出产品的质量。
3.
Methods: A random, single blind, positive-control and multi-center clinical trial recruited 230 patients with osteoarthritis, who were randomly applied onto the affected area with either piroxicam patch (n = 116) once every other day or diclofenac emulsion (n = 114) three times per day for 14 days.
方法:研究采用多中心、随机、单盲、阳性药(双氯芬酸乳胶)平行对照。
4) latexes
乳胶
1.
The results show that the rate of polymerization increases with increasing emulsifier concentration, initiator concentration and temperature, the nucleation period finishes earlier and the particle average diameter of latexes is larger than the particle produced by traditional emulsion polymerization.
对反应性乳化剂作用下的醋酸乙烯酯(VAc)乳液聚合动力学体系进行了研究,实验结果发现,聚合速率随乳化剂、引发剂浓度、温度的增大而加快,乳胶粒平均直径较传统的的乳液聚合乳胶粒子大得多,且成核期结束较早。
5) latex adhesive
乳胶
1.
The polyacrylate latex adhesives have been synthesized to meet the requirements of the development of the coated abrasives products.
根据砂布磨具对胶粘剂的性能要求 ,合成了聚丙烯酸酯乳液胶粘剂 ;考察了共聚体系中各种原料的组合、配比及用量对乳胶机械性能的影响。
6) latex
[英]['leɪteks] [美]['letɛks]
乳胶
1.
Analysis of the Water-soluble Proteins in Medical Latex Gloves
医用乳胶手套中水溶性蛋白质的含量分析
2.
The influence of the composition, ratio of network Ⅰ to network Ⅱ, the kinds and amounts of crosslinker on miscibility and damping properties of multicomponent latex interpenetrating polymer networks (LIPNs) were investigated with a rheovibron viscoelastometer.
用动态粘弹谱仪研究多组分乳胶ＩＰＮ’ｓ 体系网络的组成、配比、交联剂品种及用量等因素对体系相容性及阻尼性能的影响。
3.
The super microstructure of the outer coating of some natural latex catheters made in China and abroad with TEM was described.
用透射电镜（ＴＥＭ）观察研究了国内外几种天然乳胶导尿管外涂层的超微结构，并与其性能作了比较，结果表明，涂层的厚度和均匀度及对胶层的渗透程度直接影响产品的使用性能。
补充资料：MBS
甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物是由苯乙烯、甲基丙烯酸甲酯与丁苯胶乳进行乳液接枝而制得。 浅稻草黄色颗粒。相对密度1. 09-1．11。强度较高．刚性大，能在85-90 ℃下保持足够的刚性。低温性好，在-40 ℃下仍有良好的韧性。透明性优良，透光率可达80％-90％。热变形温度84℃(1．82MPa)。耐油、耐弱酸、耐弱碱，溶于丙酮、苯、甲苯、二氯乙烷等有机溶剂。
贮存于阴凉、通风、干燥的库房内，防火、防潮。
相对密度 1．07
透光率 85％
折射率 1．538
仲长率 ＞12％
拉伸强度 ＞38．42MPa
缺口冲击强度(23℃）＞28.03kJ/m2
洛氏硬度 100
贮存于阴凉、通风、干燥的库房内，防火、防潮。
相对密度 1．07
透光率 85％
折射率 1．538
仲长率 ＞12％
拉伸强度 ＞38．42MPa
缺口冲击强度(23℃）＞28.03kJ/m2
洛氏硬度 100