1) wet grinding ratio
润磨比
2) damp milling
润磨
1.
Improving coal-based direct reduction of magnetite pellets by damp milling;
磁铁矿球团煤基直接还原工艺中润磨的强化
2.
Experiment on damp milling process parameters of pelletizing in MaSteel
马钢球团润磨工艺试验研究
3.
However its surface characteristics and sintering capability can be improved through damp milling or mixing with limestone.
巴西镜铁精粉难制粒反应性差,通过润磨单一镜铁矿或其与石灰石的混合料可改善其表面性质和高温反应性能。
3) humidifying grinder
润磨
1.
Some advanced technologies, such as new type humidifying grinder, large type granulating disk and green pellets reforming new flowsheet etc.
介绍了济钢4号14m2球团竖炉的工艺设计特点,设计不仅完善了球团厂4座竖炉公辅设施,还开发了具有济钢自主知识产权的第二代润磨机技术、第二代7。
2.
The design features of LINFEN I&S Co 8?m 2 pelletizing shaft furnace were presented This design was considered as perfect because of adopting humidifying grinder,secondery cooling,shuttle distributor etc advanced technologies,and equipted with complete automatic control and efficient precipitation syste
介绍了临钢 8m2 球团竖炉设计 ,其工艺完善 ,采用了润磨、二次冷却、布料等先进技术 ,具有高水平的自动化控制和完善的除尘系
4) wetting grinding
润磨
1.
The production process control, pellet quality and economic benefit of our 8 m~2 shaft furnace pellet line after being added with wetting grinding are introduced, with which the fineness of iron concentrates can be reduced from 70 to 50 percent, proportion rate of bentonite decreased by 2.
介绍了承德建龙钢铁公司8m2竖炉球团生产线增加润磨工艺后,从生产过程控制、球团质量、经济效益等方面的情况,应用润磨工艺可以使铁精粉的细度(-200目)由70%下降到50%,膨润土配比降低2 5%、球团品位上升1 5%,经济效益很好。
2.
Based on trial production the influence of wetting grinding ratio of raw material on strength of pellet is studied: in laboratory roasting tests under different temperature are conducted,normal-temperature compressive strengths of pellet with different wetting grinding ratio measured,change law of hot strength of pellet in oxidizing roasting researched.
通过生产试验,研究了原料润磨比对生球强度的影响,在实验室进行了不同温度的焙烧试验,测量了原料不同润磨比时球团矿的常温抗压强度,研究了球团矿氧化焙烧过程中热态强度的变化规律。
5) wet-grinding
润磨
1.
Meanwhile wet-grinding process was studied, the results showed that wet-grinding was propitious to form bentonite fiber, and it could improve the strength of raw iron ores ball, decrease the usage of bentonite, improve the strength of preheated iron ores ball and finished product ball.
本文从机理方面详尽介绍了膨润土对球团性能的影响,并在文章中引入了膨润土纤维结构的观点,同时对润磨工艺进行了研究,结果表明:润磨有利于纤维结构的形成,可提高生球强度,降低膨润土用量和提高预热球、成品球的强度。
2.
The effects of wet-grinding on the quality of wet pellet, preheated pellet and fired pellets were studied in this paper.
研究了润磨预处理对生球强度、生球爆裂温度、预热球强度和成品球质量的影响。
6) wet grinding
润磨
1.
The result showed that the strength of preheated and fired pellet was increased by wet grinding and adding additives.
试验结果表明,润磨、加入添加剂能有效提高球团强度。