1)  polymer ferric aluminium sulfate chloride
聚合双酸铁铝
1.
The coagulant of polymer ferric aluminium sulfate chloride(PFASC) was made with pyrites cinder and sulfuric acid and chlorhydric acid as raw materials when some additives were used as lacquer solvent and stabilizer agent.
通过对造纸废水的混凝试验,考察了聚合双酸铁铝的混凝性能。
2)  polyaluminum ferric chloride sulfate
聚合双酸铝铁
1.
In this paper,the authors use polyaluminum ferric chloride sulfate(PAFCS) as a coagulant for dyeing wastewater treatment,and mainly research the effect of mixing speed,mixing time,pH,the coagulant dosage and time of coagulation for dyeing wastewater treatment by using PAFCS,thus determine the best process parameters.
选用聚合双酸铝铁作为混凝剂对该废水进行处理,主要研究搅拌速度、搅拌时间、pH值、投药量和沉降时间对聚合双酸铝铁混凝效果的影响,由此确定其最佳工艺参数。
3)  PAFS
聚合硫酸铝铁
1.
Poly Aluminum Ferric Sulfate(PAFS) was synthesized using ferrous sulfate,concentrated sulfuric acid and aluminium hydroxide as raw materials and hydrogen peroxide as the oxidant.
以硫酸亚铁、H2SO4,Al(OH)3等为原料,在氧化剂H2O2存在下合成聚合硫酸铝铁(PAFS),以n(Fe):n(Al)为影响因素,调整FeSO4。
2.
Present the investigation of the optimal parameters of coagulant paper making wastewater treatment with PAFS as coagulant and PAM as coagulant aid by orthogonal process.
通过聚合硫酸铝铁PAFS和助凝剂聚丙烯酰胺PAM对造纸废水处理效果的研究,表明在溶液pH值为5,PFS投加量为1000mg/L,PAM的用量为2。
3.
Then a Na_2CO_3 solution was slowly added to the acid solution to prepare the poly aluminum ferric sulfate(PAFS).
本文以火电厂排放的固体废弃物——粉煤灰为原料,利用酸溶和碱溶提取其中有用的Al、Fe、Si元素,并将得到的Al、Fe盐溶液通过慢速滴碱法研制出了聚合硫酸铝铁(PAFS)。
4)  PSAF
聚合硅酸铝铁
1.
On the Treatment of Domestic Sewage by PSAF Flocculant;
聚合硅酸铝铁絮凝剂处理生活污水的研究
2.
The PSAF floccule is produced with sulfate aluminum, sulfate iron and water glass as the main material.
以硫酸铝、硫酸铁、水玻璃为主要原料制备了聚合硅酸铝铁(PSAF)絮凝剂。
3.
Based on aluminium sulphate,ferric sulphate and silicic acid,polysilicate aluminium ferric (PSAF) being used as a flocculant has been synthesized.
以硫酸铝、硫酸铁、水玻璃为主要原料 ,制备了聚合硅酸铝铁 (PSAF)絮凝剂。
5)  poly-ferric aluminum silica sulfate
聚合硫酸铁铝硅
1.
A new composite poly-ferric aluminum silica sulfate (PFASS) coagulant is prepared by using pyrite residual, calcium aluminates, water glass, and sulphuric acid as raw materials and through acidic leachig, neutralization, and polymerization.
研究以硫铁矿烧渣、铝酸钙粉、水玻璃、硫酸为原料,通过酸溶、中和、聚合过程,制备新型复合混凝剂———聚合硫酸铁铝硅(PFASS)的方法。
2.
A new type of inorganic polymer coagulant,poly-ferric aluminum silica sulfate(PFASS),was prepared by using fly ash,crap iron and waste sulfuric acid as raw materials under the conditions of reaction temperature 95—90℃,reaction time 3h,liquid solid ratio 3.
10的条件下,制备出了新型无机高分子混凝剂-聚合硫酸铁铝硅(PFASS),并对其混凝性能、晶形貌像和形态分布进行了研究。
6)  poly-silicate ferric-aluminum(PSFA)
聚合硅酸铁铝
1.
A new poly-silicate ferric-aluminum(PSFA)was prepared by using water glass,ferric chloride and aluminum sulfate as raw materials.
以硫酸铝、三氯化铁、水玻璃为主要原料制备无机高分子水处理剂聚合硅酸铁铝(PSFA)。
补充资料:硫铝酸盐水泥和铁铝酸盐水泥


硫铝酸盐水泥和铁铝酸盐水泥
sulPhoaluminateCement and ferralUminate eement

  硫铝酸盐水泥和铁铝酸盐水泥Sulphoaluminatecement and ferraluminate eement以石灰石、矾土(SAC为铝矾土,FAC为铁钒土)和石膏为原料制成的水泥。原料在回转窑中低温缎烧成以C4A3S、CZS和C6AF:(或C;AF)为主要矿物组成的熟料,通过掺入适量掺合料并共同粉磨而成水泥。为区别于硅酸盐水泥(第一系列)、铝酸盐水泥(第二系列)而将其称为第三系列水泥。 硫铝酸盐(S AC)水泥和铁铝酸盐(F AC)水泥由中国研制成功,并分别于1974年和1983年投入工业生产。目前生产的SAC类水泥品种有快硬、高强、膨胀、自应力和低碱硫铝酸盐水泥(GRC专用水泥);FAC类水泥品种有快硬、高强、膨胀和自应力铁铝酸盐水泥。 硫铝酸盐水泥和铁铝酸盐水泥具有以下特性:①较高的早期强度,而且具有不断增长的后期强度和满足使用要求的凝结时间,12小时至1天的抗压强度可达35一60 MPa,抗折强度达6.5一7.SMPa;其高强水泥3天抗压强度可达80一100 MPa,抗折强度达9.0一11.OMPa。②膨胀性能可在很大范围内调节。根据实际应用需要,其砂浆自由膨胀可在0.05一1.5%之间调节,其自应力值可在0.5一5.OMPa之间调节。③在0一10oC低温下使用,其早期强度(1一3天)是同标号硅酸盐水泥混凝土的5一10倍。在0一一20aC低温下使用,加入少量外加剂,3一7天的混凝土强度可达设计标号的70一80%。在正、负温交替条件下施工,对后期强度增长影响不大。实验室300次冻融循环,混凝土强度损失不明显。④水泥石结构较致密,其混凝土抗掺性是同标号硅酸盐水泥混凝土的2一3倍。⑤对海水、氯盐(NaCI,MgC12)、硫酸盐(NaZSO‘、MgSO‘、(NH‘)250小尤其是它们的复合盐类(MgSO‘+NaCI),均具有很好的抗腐蚀性。其中铁铝酸盐水泥类更优于硫铝酸盐水泥类。⑥硫铝酸盐水泥类混凝土因早期(前3天)水化液相碱度较低,钢筋有轻微锈蚀。随时间的推移,水泥水化液相碱度提高,水泥石微结构致密,因此后期锈蚀情况无发展。而铁铝酸盐水泥由于水化液相碱度较高,对钢筋无锈蚀。 第三系列水泥适用于各种建筑工程,预应力混凝土构件和水泥制品。特别适用于地下工程、海港工程、抢修和抢建工程,制作自应力水泥压力管,高强管、桩和各种GRC制品。(苏慕珍)
  