1) ACHF
活性中空炭纤维
1.
The adsorption capacity to iodine and methylene blue of the resultant activated hollow carbon fibers (ACHF) were tested.
聚丙烯腈(PAN)中空纤维在空气中、不同温度下预氧化2h,接着在N2气氛中炭化,CO2气氛中活化,得到PAN基活性中空炭纤维(PANACHF)。
2.
The adsorption properties of PAN-Based ACHF produced at different condition to creatinine, VB12 and bilirubin are tested.
用不同浓度的 (NH4)2HPO4溶液和不同浸渍时间处理过的聚丙烯腈 (PAN) 基中空纤维在空气中270℃预氧化,并在N2气氛下于700℃炭化,随后用CO2气体在800℃活化,测定了PAN基活性中空炭纤维对肌酐、VB12和胆红素的吸附量。
2) activated carbon hollow fiber
活性中空炭纤维
1.
Influence of carbonization process on polyacrylonitrile-based activated carbon hollow fiber;
炭化过程对聚丙烯腈基活性中空炭纤维性能的影响
2.
Effect of activation temperature on structure and adsorptivity of polyacrylonitrile-based activated carbon hollow fiber;
活化温度对聚丙烯腈基活性中空炭纤维结构和吸附性能的影响
4) polyacrylonitrile activated carbon hollow fiber
PAN基中空活性炭纤维
5) active carbon fiber-nanometer silver
中空活性炭纤维-纳米银
1.
Application of active carbon fiber-nanometer silver dressing on the infected surface;
中空活性炭纤维-纳米银敷料对感染创面作用的初步报告
6) Mesoporous ACF
中孔活性炭纤维
补充资料：中空活性炭纤维
分子式：
CAS号：
性质：具有吸附和半透膜功能的特种纤维。主要品种是聚乙烯醇系，比表面积1450～2730m2/g，中空部最大直径5.3～9.7μm，中空率13～78％(体积)，纤维外径11.5～12.5μm，苯吸附量65％～110％。制法是将工业用2000dtex/1000根聚乙烯醇纤维，强度9.2cN/dtex，伸长率7％，用一定浓度(NH4)2SO4+(NH4)2HPO4、H2SO4、ZnCl2或H3PO4各选其一处理后，在400～900℃热处理，再于1050～1100℃水蒸气活化而得。用于臭氧分解、糖液脱色和精制、有机物高精度吸附和分离、空气的氧氮分离、乙醇和水分离等。
CAS号：
性质：具有吸附和半透膜功能的特种纤维。主要品种是聚乙烯醇系，比表面积1450～2730m2/g，中空部最大直径5.3～9.7μm，中空率13～78％(体积)，纤维外径11.5～12.5μm，苯吸附量65％～110％。制法是将工业用2000dtex/1000根聚乙烯醇纤维，强度9.2cN/dtex，伸长率7％，用一定浓度(NH4)2SO4+(NH4)2HPO4、H2SO4、ZnCl2或H3PO4各选其一处理后，在400～900℃热处理，再于1050～1100℃水蒸气活化而得。用于臭氧分解、糖液脱色和精制、有机物高精度吸附和分离、空气的氧氮分离、乙醇和水分离等。