1) low temperature carbonization
低温碳化
1.
This paper introduces the way of preparing nanocystalline WC which average grain size is about 20-30nm and average particle size is less than 100nm with low temperature carbonization method,and the WC powder is tested by composition analysis,DSC,XRD,SEM and BET method.
本文主要讲述了用低温碳化的方法制备平均晶粒度为20~30nm,颗粒尺寸小于100 nm的纳米碳化钨粉末。
2.
Nanocystalline WC powder was prepared by low temperature carbonization.
利用成分分析和XRD,SEM以及BET等检测手段,对低温碳化工艺制备纳米级WC粉末进行了研究,制备了平均晶粒度在20~30 nm,颗粒尺寸小于100 nm的纳米碳化钨粉末。
2) low temperature carbonization furnace
低温碳化炉
3) zone of low temperature cabonization
低温碳化层
4) low temperature carbonization
低温碳化处理
5) low-temperature CNTs
低温碳管
6) Low temperature carburizing
低温渗碳
1.
Low temperature carburizing process tests on 20~#、20Cr、20CrMnTi、20MnVB steels;
20~#20Cr、20CrMnTi、20MnVB钢的低温渗碳工艺试验
2.
In this paper a fast developing method is made comprehensive review for hardening surface of austenite stainless steels without any reduction of corrosion resistance,which is called austenite stainless steels low temperature carburizing.
本文综合评述了一种近年来发展较快的不影响奥氏体不锈钢耐蚀性能的表面强化工艺--奥氏体不锈钢低温渗碳技术,论述了该技术的工艺特点,探讨了该技术的强化原理,并预测了它的发展前景。
补充资料：碳化硅晶须补强碳化硅陶瓷基复合材料
分子式：
CAS号：
性质：以碳化硅陶瓷为基和以碳化硅晶须为增强剂的新型陶瓷材料。通过晶须的载荷转移、拔出及裂纹偏转作用，获得比普通碳化硅更高的强度和韧性。使用温度达1400℃。是一种重要的高温结构陶瓷。用于燃气轮机叶片等高温部件和耐磨件制造。采用原位生长工艺和烧结工艺制取。
CAS号：
性质：以碳化硅陶瓷为基和以碳化硅晶须为增强剂的新型陶瓷材料。通过晶须的载荷转移、拔出及裂纹偏转作用，获得比普通碳化硅更高的强度和韧性。使用温度达1400℃。是一种重要的高温结构陶瓷。用于燃气轮机叶片等高温部件和耐磨件制造。采用原位生长工艺和烧结工艺制取。