1) tensile strength
轴拉强度
1.
The main objective of the tests is to determine the relationship between the tensile strength and splitting strength of steel fiber reinforced concrete(SFRC).
分析研究了钢纤维高强混凝土的轴拉强度和劈拉强度的关系,钢纤维高强混凝土轴拉性能随钢纤维体积掺量、基体强度及钢纤维类型的变化规律。
2.
With raw materials of Jinping first-level hydropower station,the experimental study on performance of hydraulic concrete with magnesia shows that the compressive strength of concrete added with magnesia is descreased slightly and cleavage strength,tensile strength,modulus of elasticity,tensile strain ultimate of concrete added with magnesia are increased slightly.
通过采用锦屏一级水电站的原材料,对外掺氧化镁的水工混凝土性能试验研究表明,外掺氧化镁对混凝土的抗压强度略有降低,对劈拉强度、轴拉强度、弹性模量、极限拉伸值略有提高;未掺氧化镁的砂岩混凝土180d自身体积变形为-57。
2) uniaxial tensile strength
轴拉强度
1.
The uniaxial tensile strength and bending strength increase a little, but the tensile peak\|strain and the ratio of tensile\|compressive and bending\|compressive increase remarka.
试验结果表明 ,随着聚醋酸乙烯的掺入 ,砂浆的轴压强度和弹性模量显著下降 ,但极限应变却明显增大 ;砂浆的轴拉强度和抗弯强度均略有提高 ,而极限应变、拉压强度比和弯压强度比则显著增加。
3) axial tensile strength
轴拉强度
1.
The results show that the compressive strength,splitting tensile strength and axial tensile strength of RCC body are all higher than that of RCC with layer surface.
研究不同工况有层面碾压混凝土及其碾压混凝土本体强度特性 ,得出碾压混凝土本体抗压强度、劈拉强度和轴拉强度均大于有层面碾压混凝土的相应强度。
4) axial tensile strength
轴心抗拉强度
1.
The effects of steel fiber volumetric ratio,steel fiber slenderness ratio and steel fiber type on the splitting tensile strength,axial tensile strength and axial tensile stress-strain curve of steel fiber reinforced concrete(SFRC) are studied.
研究了钢纤维体积率、钢纤维长径比、钢纤维类型对钢纤维混凝土劈裂抗拉强度、轴心抗拉强度及轴心受拉应力-应变全曲线的影响规律。
2.
Discussion is given in this paper about the characteristics of axial compression strength,axial tensile strength and modulus of elastidty,which is obtained by testing non-selt buming waste concrete.
针对试验得到的非自燃煤矸石混凝土的棱柱体轴心抗压强度、轴心抗拉强度及弹性模量的特点进行了讨论,给出了相应计算表达式,并对设计取值提出了建议。
5) triaxial tensile strength
三轴抗拉强度
6) uniaxial tensile strength
单轴抗拉强度
1.
Experimental study on uniaxial tensile strength characteristic of grit stone after high temperature;
高温后粗砂岩单轴抗拉强度实验研究
补充资料:轴向强度
分子式:
CAS号:
性质:取向聚合物沿取向轴方向的强度。单轴取向的聚合物材料(如纤维)由于分子链或链段沿取向方向定向排列,其轴向拉伸强度很高。单轴取向的薄膜(如撕裂薄膜),其轴向强度较高,而垂直取向方向的强度却极差;双轴取向的薄膜,则在膜平面的任何方向都具有较高的强度。
CAS号:
性质:取向聚合物沿取向轴方向的强度。单轴取向的聚合物材料(如纤维)由于分子链或链段沿取向方向定向排列,其轴向拉伸强度很高。单轴取向的薄膜(如撕裂薄膜),其轴向强度较高,而垂直取向方向的强度却极差;双轴取向的薄膜,则在膜平面的任何方向都具有较高的强度。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条