The new reactive flame retardant 2,4,6 tribromo N,N bis (2 hydroxylethyl) aniline was prepared with aniline, epoxy ethane and bromine as the raw materials.

以苯胺、环氧乙烷和溴素为原料 ,研究了新反应型阻燃剂 N,N-二 ( 2 -羟乙基 ) - 2 ,4,6-三溴苯胺的合成方法 ,用红外光谱和元素分析等方法确认了其化学结构。

更多例句>>

4) flame retarding reaction 点击朗读

阻燃反应

5) reactive phosphorus flame retardant 点击朗读

反应型磷系阻燃剂

This paper describes the synthesis of reactive phosphorus flame retardants bis (4 -carboxyphenyl) phenyl phosphine oxide ( BCPPO), bis(4 -hydroxyphenyl) phenyl phosphine oxide (BHPPO) , etc and phosphorus-containing flame retardant Nylon 66 copolymers,co-polycarbonates and polyarylates as well as the flame retardant performances of these three kinds of polymers mentioned above.

叙述反应型磷系阻燃剂双(4-羧苯基)苯基氧化膦和双(4-羟苯基)苯基氧化膦等的合成,以及以三芳基氧化膦为链段的含磷阻燃尼龙66共聚物、共聚碳酸酯及聚芳酯的合成方法,讨论了按上述方法合成的阻燃工程塑料的阻燃性能。

6) fire-retardant modifier 点击朗读

阻燃改性剂

This paper,based on the analysis of the existing research achievements at home and abroad,developed the fire-retardant modifier and modified fire-retardant asphalt and proposed their processing technique.

在分析总结国内外已有的相关研究成果的基础上,结合隧道内具体的使用环境,开发研究了沥青阻燃改性剂及阻燃改性沥青,并提出了它们的生产工艺。

补充资料：用氢氧化镁作阻燃剂制备阻燃PP的方法

聚丙烯（PP）以其密度小、力学性能好、耐化学腐蚀、易加工、耐热变形温度高、价格低廉等突出优点，在许多行业得到了广泛的应用。阻燃PP已成为使用阻燃剂量最大、增长最快的高聚物阻燃材料。氢氧化镁［Mg(OH)2］作为一种无卤阻燃剂，除能阻燃外还有消烟性能，而且脱水温度高，比较适于加工温度较高的PP等高聚物阻燃改性，在降低对环境的危害和材料安全处理方面更能满足有关法规的要求，同时也使阻燃塑料更易于再生利用。特别是Mg(OH)2原料来源丰富，价格低廉，用它作为PP的阻燃剂有较高的经济效益，所以近年全国各地对用Mg(OH)2阻燃PP十分重视。

然而目前多数企业在用Mg(OH)2阻燃PP时，由于Mg(OH)2用量不足，需添加其他阻燃剂，致使配方成本居高不下。为此，笔者谈一下在用Mg(OH)2作PP阻燃剂时应注意的一些事项。用Mg(OH)2阻燃PP时，为使材料达到ＵＬ94Ｖ-０阻燃级（3.2ｍｍ试样），用量应≥60%，不过，如用Mg(OH)2抑烟，则用量可低一些，含40%Mg(OH)2的PP的烟密度仅为未阻燃PP的约1/3。当PP中Mg(OH)2含量达65时，其机械性能，特别是抗冲强度和伸长率均显著劣化。为了使Mg(OH)2阻燃PP材料的力学性能不至下降很多，应选择粒径微细、粒径分布窄而均匀的Mg(OH)2作原料，并进行双偶联表面处理，以改善物料的流变性能，促进混炼加工时通过Mg(OH)2／PP表面导热而避免形成局部热点，并提高Mg(OH)2与PP的相容性，使其能在聚合物中较均匀地分散。

采用这种经处理的Mg(OH)2阻燃PP时，在对PP作增韧改性后，即使高Mg(OH)2含量的阻燃PP也可获得良好的加工性能及物理机械性能。为使Mg(OH)2在PP中均匀分散，可用布斯捏合机（ＢｕｓｓＫｅｎａｄｅｒ），或德国产双螺杆混炼挤出机，或往复式单螺杆混炼挤出机来进行混炼，并采用合理的加料混合混炼方式。例如，可将全部PP及增韧剂与所需量60%的Mg(OH)2第一次加入混合混炼机中先混合混炼数分钟后，再第二次加入余下的Mg(OH)2。

在加料时应注意加料要均匀，计量要准确。若采用密炼机混炼，对Mg(OH)2除采用两次加入法外，还要准确计量装料率在87%～93%范围内较好。当装料率较少时，混炼效果差，当装料率＞95%时，易造成Mg(OH)2凝集结团，难以分散均匀。混炼不均匀不仅使阻燃性能降低，而且拉伸强度和断裂伸长率都降低，制品外观也较差。总之，采用对PP良好的增韧改性，用经特殊表面处理并对粒径及粒度分布控制的Mg(OH)2，采用适宜的混炼机械及两次加料方法，可使Mg(OH)2在PP中分散均匀。这种阻燃PP可兼具很多应用领域所需材料的机械性能及阻燃性能，还具有抑烟、低毒、无卤、不用Ｓｂ2Ｏ３，环境友好，配方成本低的特点，有较高的经济效益和社会效益。

说明：补充资料仅用于学习参考，请勿用于其它任何用途。

参考词条

硅系改性阻燃剂耐久性阻燃剂增效性阻燃剂阻燃性增塑剂反应性溶剂反应性试剂燃烧反应特性

活性阻燃剂反应阻止剂阻燃剂供应员燃烧反应性燃料反应性

说明：双击或选中下面任意单词，将显示该词的音标、读音、翻译等；选中中文或多个词，将显示翻译。
	您的位置：首页 -> 词典 -> 反应性阻燃剂 1) Reactive flame retardant 反应性阻燃剂 2) reactive flame retardant 反应阻燃剂 3) reactive flame retardant 反应型阻燃剂 1. The new reactive flame retardant 2,4,6 tribromo N,N bis (2 hydroxylethyl) aniline was prepared with aniline, epoxy ethane and bromine as the raw materials. 以苯胺、环氧乙烷和溴素为原料 ,研究了新反应型阻燃剂 N,N-二 ( 2 -羟乙基 ) - 2 ,4,6-三溴苯胺的合成方法 ,用红外光谱和元素分析等方法确认了其化学结构。更多例句>> 4) flame retarding reaction 阻燃反应 5) reactive phosphorus flame retardant 反应型磷系阻燃剂 1. This paper describes the synthesis of reactive phosphorus flame retardants bis (4 -carboxyphenyl) phenyl phosphine oxide ( BCPPO), bis(4 -hydroxyphenyl) phenyl phosphine oxide (BHPPO) , etc and phosphorus-containing flame retardant Nylon 66 copolymers,co-polycarbonates and polyarylates as well as the flame retardant performances of these three kinds of polymers mentioned above. 叙述反应型磷系阻燃剂双(4-羧苯基)苯基氧化膦和双(4-羟苯基)苯基氧化膦等的合成,以及以三芳基氧化膦为链段的含磷阻燃尼龙66共聚物、共聚碳酸酯及聚芳酯的合成方法,讨论了按上述方法合成的阻燃工程塑料的阻燃性能。 6) fire-retardant modifier 阻燃改性剂 1. This paper,based on the analysis of the existing research achievements at home and abroad,developed the fire-retardant modifier and modified fire-retardant asphalt and proposed their processing technique. 在分析总结国内外已有的相关研究成果的基础上,结合隧道内具体的使用环境,开发研究了沥青阻燃改性剂及阻燃改性沥青,并提出了它们的生产工艺。补充资料：用氢氧化镁作阻燃剂制备阻燃PP的方法聚丙烯（PP）以其密度小、力学性能好、耐化学腐蚀、易加工、耐热变形温度高、价格低廉等突出优点，在许多行业得到了广泛的应用。阻燃PP已成为使用阻燃剂量最大、增长最快的高聚物阻燃材料。氢氧化镁［Mg(OH)2］作为一种无卤阻燃剂，除能阻燃外还有消烟性能，而且脱水温度高，比较适于加工温度较高的PP等高聚物阻燃改性，在降低对环境的危害和材料安全处理方面更能满足有关法规的要求，同时也使阻燃塑料更易于再生利用。特别是Mg(OH)2原料来源丰富，价格低廉，用它作为PP的阻燃剂有较高的经济效益，所以近年全国各地对用Mg(OH)2阻燃PP十分重视。然而目前多数企业在用Mg(OH)2阻燃PP时，由于Mg(OH)2用量不足，需添加其他阻燃剂，致使配方成本居高不下。为此，笔者谈一下在用Mg(OH)2作PP阻燃剂时应注意的一些事项。用Mg(OH)2阻燃PP时，为使材料达到ＵＬ94Ｖ-０阻燃级（3.2ｍｍ试样），用量应≥60%，不过，如用Mg(OH)2抑烟，则用量可低一些，含40%Mg(OH)2的PP的烟密度仅为未阻燃PP的约1/3。当PP中Mg(OH)2含量达65时，其机械性能，特别是抗冲强度和伸长率均显著劣化。为了使Mg(OH)2阻燃PP材料的力学性能不至下降很多，应选择粒径微细、粒径分布窄而均匀的Mg(OH)2作原料，并进行双偶联表面处理，以改善物料的流变性能，促进混炼加工时通过Mg(OH)2／PP表面导热而避免形成局部热点，并提高Mg(OH)2与PP的相容性，使其能在聚合物中较均匀地分散。采用这种经处理的Mg(OH)2阻燃PP时，在对PP作增韧改性后，即使高Mg(OH)2含量的阻燃PP也可获得良好的加工性能及物理机械性能。为使Mg(OH)2在PP中均匀分散，可用布斯捏合机（ＢｕｓｓＫｅｎａｄｅｒ），或德国产双螺杆混炼挤出机，或往复式单螺杆混炼挤出机来进行混炼，并采用合理的加料混合混炼方式。例如，可将全部PP及增韧剂与所需量60%的Mg(OH)2第一次加入混合混炼机中先混合混炼数分钟后，再第二次加入余下的Mg(OH)2。在加料时应注意加料要均匀，计量要准确。若采用密炼机混炼，对Mg(OH)2除采用两次加入法外，还要准确计量装料率在87%～93%范围内较好。当装料率较少时，混炼效果差，当装料率＞95%时，易造成Mg(OH)2凝集结团，难以分散均匀。混炼不均匀不仅使阻燃性能降低，而且拉伸强度和断裂伸长率都降低，制品外观也较差。总之，采用对PP良好的增韧改性，用经特殊表面处理并对粒径及粒度分布控制的Mg(OH)2，采用适宜的混炼机械及两次加料方法，可使Mg(OH)2在PP中分散均匀。这种阻燃PP可兼具很多应用领域所需材料的机械性能及阻燃性能，还具有抑烟、低毒、无卤、不用Ｓｂ2Ｏ３，环境友好，配方成本低的特点，有较高的经济效益和社会效益。说明：补充资料仅用于学习参考，请勿用于其它任何用途。参考词条硅系改性阻燃剂耐久性阻燃剂增效性阻燃剂阻燃性增塑剂反应性溶剂反应性试剂燃烧反应特性

©2011 dictall.com