1) borosilicate glass
高硼硅玻璃
1.
The control of production technology parameters is difficulty due to high melting temperature of borosilicate glass and volatility of boron .
高硼硅玻璃由于熔化温度高、硼易于挥发等原因,在实际中难于操作控制。
2) Pyrex glass
高硼硅玻璃
1.
Pyrex glass is a kind of borosilicate which contains above 78% SiO_2 and 13% B2O3.
高硼硅玻璃是指SiO_2>78%,B_2O_3>10%的硼硅酸盐玻璃。
3) borosilicate glass
硼硅玻璃
1.
Microstructure and properties of borosilicate glass coating for oxidation protection of C/SiC brake materials;
C/SiC刹车材料硼硅玻璃防氧化涂层的结构与性能
2.
Mechanisms of anodic bonding between borosilicate glass and silicon;
硼硅玻璃与硅阳极键合机理分析
3.
The mechanisms of anodic bonding between borosilicate glass and silicon;
硼硅玻璃与硅阳极键合界面形成机理分析
4) borosilicate glass
硅硼玻璃
1.
The wettability of borosilicate glass on Kovar with oxides of FeO and FeO+Fe3O4 respectively was studied as a function of holding time at 1000℃ by the sessile drop method.
采用座滴法研究硅硼玻璃在分别具有FeO和FeO+Fe3O4氧化膜的可伐合金表面1000℃保温不同时间的润湿规律。
5) high boron glass
高硼玻璃
1.
The melting characteristics of high boron glass was expounded .
阐述了高硼玻璃的熔制特性,通过对窑内玻璃液流温度分布的分析,认为用全电熔窑熔化高硼玻璃比较理想,并提出了相关注意事项。
6) vycor glass
高硼硅酸耐热玻璃
补充资料：多孔高硅氧玻璃
分子式：
CAS号：
性质：一种用于从硝酸钍溶液中吸附233pa的吸附剂。它的组成为94％～96％SiO2，3％～5％B2O3，孔隙率约28％。它具有很高的化学稳定性，热稳定性和耐辐照稳定性，高导热系数和很低的水浸出率。多孔高硅氧玻璃对233pa有很强的吸附能力和吸附容量。它吸附233Pa的能力和许多因素有关：玻璃的拉度越细，吸附速度越快，分配系数也越大；分配系数随硝酸浓度提高而增加，随溶液中钍浓度和氟离子浓度的增加而下降。多孔高硅氧玻璃柱可以直接从二氧化钍的溶解液中吸附233pa，并已经过热实验验证。
CAS号：
性质：一种用于从硝酸钍溶液中吸附233pa的吸附剂。它的组成为94％～96％SiO2，3％～5％B2O3，孔隙率约28％。它具有很高的化学稳定性，热稳定性和耐辐照稳定性，高导热系数和很低的水浸出率。多孔高硅氧玻璃对233pa有很强的吸附能力和吸附容量。它吸附233Pa的能力和许多因素有关：玻璃的拉度越细，吸附速度越快，分配系数也越大；分配系数随硝酸浓度提高而增加，随溶液中钍浓度和氟离子浓度的增加而下降。多孔高硅氧玻璃柱可以直接从二氧化钍的溶解液中吸附233pa，并已经过热实验验证。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。