1) Grinding ball
磨球
1.
Analysis on worn morphology of middle and low chromium grinding balls used in wet mill;
湿式磨机中低铬铸铁磨球的磨损形貌分析
2.
The development and application of Cr-Mn-W wear-resistance cast iron on grinding ball in thermal power plant
火电厂球磨机铬锰钨抗磨铸铁磨球的研制与应用
3.
The characteristics of the impact stresses of grinding balls in ball mills and the material selection of liners
球磨机磨球冲击应力特性与衬板的选材
2) grinding balls
磨球
1.
Investigation of alloying mechanism of WMnV wear resistant cast iron and manufacturing process of grinding balls;
W-Mn-V 抗磨铸铁的合金化原理及磨球制造工艺
2.
Trooslite grinding balls of high Chromium white cast iron with RE;
托氏体稀土高铬白口铸铁磨球
3.
The EPC process used for producing of cast iron grinding balls was introduced including: chemicalcomposition of grinding balls, melting process, production of EPS patterns and ball patterns assembling process,pouring process, as well as equipment and investment.
介绍消失模铸造磨球的化学成分、熔炼工艺、磨球生产工艺流程、EPS模的制作和组串工艺,浇注工艺,以及设备和投资。
3) mill ball
磨球
1.
The operating mode and forces analysis of mill ball in the mill;
球磨机中磨球的工作状况及受力分析
2.
This item points to present problems, from chemical on situation, micro organization, forming shaping technology and product proceeding, new design is conducted, by metallography, hardness test, tiredness test; mill bass are investigated, result indicates that this mill ball has good wear-resistant behavior, long using ago and low cos
针对目前磨球存在的问题,从化学成分、显微组织、成型技术、加工处理工艺进行新的设计,并通过金相,硬 度测试,疲劳实验对磨球进行检测。
4) milling ball
磨球
1.
The effects of heat treatment process parameters of the step austempering in room-temperature machine oil on the structure and properties of the low alloy bainite ductile iron for milling ball have been studied.
研究了室温油分级等温淬火热处理工艺参数对低合金贝氏体球墨铸铁磨球组织和性能的影响。
2.
The change of grain size of Cr, Al,Cu and Cr 20 Al 80 powders during ball milling and the forming law of the surface coating of milling balls were investigated.
研究了Cr粉、Al粉、Cu粉、Cr2 0 Al80 粉末球磨过程中粉末粒度尺寸的变化以及磨球表面涂层的形成规律 ,结果发现 ,磨球表面涂层的形成与粉末细化之间有一定的关系。
3.
Through reviewing all kinds of materials which can manufacture the milling balls at present in our country, it finds that milling ball maked by low chromium cast is suit to the wear environments in waterish grindi.
通过对目前使用的磨球材质进行综合考察,以磨球的性价比为标准,认为低铬铸铁磨球是一种适合于金属矿山湿式球磨机磨损工况的磨球。
5) ball mill
球磨
1.
Preparation of ultrafine α′-Fe(N) powders by ball mill method;
球磨法制备α′-Fe(N)超细粉末
2.
The application of fuzzy-PID control to a concentration process for ball milling density;
模糊PID在选矿球磨浓度控制中的应用
3.
The Fe-Co-Nb-B nanocrystalline powders were mechanically alloyed with a vibrational high energy ball mill.
采用机械合金化方法,在摆振式高能球球磨机上制备Fe-Co-Nb-B纳米晶合金粉末,计算球磨后应力带来的晶格畸变对X射线衍射峰宽化的影响。
6) ball-milling
球磨
1.
The Variation in the Crystal Structure of Wollastonite During Ball-milling;
硅灰石球磨过程中晶体结构的变化
2.
The structure and properties of spinel LiMn_2O_4 with ball-milling treatment;
球磨处理尖晶石相LiMn_2O_4的结构及性能
3.
The Design of a ball-milling Mud Settlement Rate Measure Sensor;
一种球磨泥浆沉降速率测量传感器的设计
补充资料：铸态高铬屈氏体磨球的生产
摘要：本文从优化成分设计、熔炼、变质处理、铸造及热处理等工艺控制措施入手，综合介绍了铸态高铬屈氏体磨球的生产过程，并经生产试验使各工艺参数达最佳匹配，为生产出高质量的铸态高铬屈氏体磨球提供了强有力的理论支撑。
关键词：高铬屈氏体磨球 优化 工艺控制
含铬大于11%的铬系白口铸铁成为高铬铸铁，马氏体Cr15高铬铸铁是目前国内外广泛应用的较典性的耐磨铸铁，用于制造磨球、衬板等，取得了较好的节材降耗效果。马氏体高铬铸铁磨球具有较高的硬度，但韧性较差。马氏体Cr15磨球是经热处理淬火加回火的工艺获得的，因此需要一套专用的热处理设备。这不仅投资及能源消耗大、生产周期长、生产成本也较高，从而影响了它的广泛应用。
我们的目的是研制一种既有高铬铸铁的耐磨性和韧性，生产工艺简单、成本低廉的材料：铸态高铬屈氏体磨球。它与淬火马氏体Cr15磨球相比，具有省工、省时、省能耗、省原材料消耗的的优势。它的生产应用能产生较大的社会效益。
一．成分设计
碳：碳为生成共晶碳化物（Cr·Fe）7C3的主要元素，共晶碳化物在耐磨性方面起着重要作用。碳含量决定碳化物的数量。选择较高的碳含量，可获得较多的高硬度碳化物。为提高耐磨性，碳的质量分数应控制在2.8～3.1%。
铬：铬含量决定碳化物的类型。为保证碳化物以M7C3为主，铬含量必须大于12%，过低不能形成高硬度的（Cr·Fe）7C3型碳化物；过高则成本提高。因此铬的质量分数为12～14%。
关键词：高铬屈氏体磨球 优化 工艺控制
含铬大于11%的铬系白口铸铁成为高铬铸铁，马氏体Cr15高铬铸铁是目前国内外广泛应用的较典性的耐磨铸铁，用于制造磨球、衬板等，取得了较好的节材降耗效果。马氏体高铬铸铁磨球具有较高的硬度，但韧性较差。马氏体Cr15磨球是经热处理淬火加回火的工艺获得的，因此需要一套专用的热处理设备。这不仅投资及能源消耗大、生产周期长、生产成本也较高，从而影响了它的广泛应用。
我们的目的是研制一种既有高铬铸铁的耐磨性和韧性，生产工艺简单、成本低廉的材料：铸态高铬屈氏体磨球。它与淬火马氏体Cr15磨球相比，具有省工、省时、省能耗、省原材料消耗的的优势。它的生产应用能产生较大的社会效益。
一．成分设计
碳：碳为生成共晶碳化物（Cr·Fe）7C3的主要元素，共晶碳化物在耐磨性方面起着重要作用。碳含量决定碳化物的数量。选择较高的碳含量，可获得较多的高硬度碳化物。为提高耐磨性，碳的质量分数应控制在2.8～3.1%。
铬：铬含量决定碳化物的类型。为保证碳化物以M7C3为主，铬含量必须大于12%，过低不能形成高硬度的（Cr·Fe）7C3型碳化物；过高则成本提高。因此铬的质量分数为12～14%。