1) alumina-carbon
铝碳
1.
Support vector machine, a new computational method that have powerful prediction ability and can avoid over-fitting, has been used for optimizing processing parameters (content, particle size, and firing temperature of added silicon) in the preparation of alumina-carbon material and establishing the model of their influence on cold crushing strength of samples.
采用可限制过拟合及有较强预报能力的支持向量机算法(SVM)对铝碳材料的工艺参数进行优化。
2) carbon-aluminum-carbon
碳-铝-碳
1.
Ultracapacitor contains carbon-aluminum-carbon material.
超电容电极——碳-铝-碳材料的一次成形加工质量是影响超电容电压保持性的主要因素,由传统冲裁加工所得的电极易产生毛刺、塌边以及侧面没有绝缘等问题,会引起电场的过度集中、破坏或降低隔膜层的绝缘性能,造成较大的漏电流,降低自我放电特性,影响超电容的性能稳定性和成品率,制约超电容的普及和应用。
4) titanium aluminum carbide
钛碳化铝
5) aluminizing carbon steel
渗铝碳钢
1.
The influence on aluminizing carbon steel of temperature,partial pressure of CO2,mineralization and pH value was studied through zero-G test.
在高压釜中对N80钢和渗铝碳钢材料进行了CO2腐蚀试验。
补充资料：铝碳砖
分子式：
CAS号：
性质：以Al2O3和C为主要成分的含Al2O335％～85％，含C7％～35％的耐火材料。可分为烧成砖和不烧砖两大类。铝碳砖耐火度高，化学稳定性良好，耐侵蚀。如在配料中添加ZrO2，能获得良好的抗热震性。含Al2O372％～85％、C7％～8％的烧成铝碳砖的耐压强度可达110～120MPa，1400℃抗弯强度达25MPa；含Al2O335％～46％、C+SiC30％～37％的烧成铝碳砖的耐压强度为21～28MPa。铝碳砖主要用作滑动水口滑板、连铸中间包整体塞棒等，也可用作铁水预处理用包衬和盛钢桶内衬等。
CAS号：
性质：以Al2O3和C为主要成分的含Al2O335％～85％，含C7％～35％的耐火材料。可分为烧成砖和不烧砖两大类。铝碳砖耐火度高，化学稳定性良好，耐侵蚀。如在配料中添加ZrO2，能获得良好的抗热震性。含Al2O372％～85％、C7％～8％的烧成铝碳砖的耐压强度可达110～120MPa，1400℃抗弯强度达25MPa；含Al2O335％～46％、C+SiC30％～37％的烧成铝碳砖的耐压强度为21～28MPa。铝碳砖主要用作滑动水口滑板、连铸中间包整体塞棒等，也可用作铁水预处理用包衬和盛钢桶内衬等。