1) MoSi_2
MoSi2
1.
This paper reviews the current research status and the development trend of MoSi_2 material and its composites.
综述了MoSi2及其复合材料的国内外研究现状和发展趋势。
2.
Changes of MoSi_2 coatings by Plasma Spraying at different heat treating process were studied.
研究了等离子喷涂单一MoSi2涂层在不同的热处理工艺条件下发生的变化,结果表明650℃保温1 h,试样出现粉化现象,验证了“Pesting”现象;750℃保温1 h试样背面出现Mo的氧化物晶体,对混合涂层的透射电镜观察证实了MoSi2的热障涂层中起到了自愈合作用。
3.
8%La_2O_3-Mo_5Si_3/MoSi_2 composites at 1200 ℃ in air was investigated.
8%La2O3-Mo5Si3/MoSi2复合材料在1200℃空气中的高温氧化行为。
2) MoSi 2
MoSi2
1.
The uniform dispersing processing of ZrO 2(n) /MoSi 2 composite powders and SiC (W) /ZrO 2(n) /MoSi 2 composite powders prepared by mixing with multiphase suspension were also discussed.
介绍了SiC晶须分散工艺,探讨了多相悬浮液混合法制备ZrO2 (n) MoSi2 复合粉体及SiC(W) ZrO2 (n) MoSi2 复合粉体的均匀混合工艺。
2.
The sintering tempera ture of MoSi 2 by MA is at least lower about 250℃than that by SHS.
利用粉末烧结理论对比分析了机械合金化(MA)和高温自蔓延(SHS)合成的MoSi2粉末的烧结性能,并阐明了原因。
3.
Microstructure of the laser cladding molybdenum silicides composite coatings consists of the primary dendritic MoSi 2,plate-like iron-molybdenum-silicide (FeMoSi) and the interdendritic MoSi 2α eutectic struc.
以Mo -Si合金粉末为原料 ,采用激光熔覆技术在奥氏体不锈钢 1Cr1 8Ni9Ti表面上制得了由初生MoSi2 树枝晶、块状FeMoSi初生相及枝晶间MoSi2 /α片层状共晶组织组成的难熔金属硅化物高温复合材料涂层。
3) molybdenum disilicide
MoSi2
1.
Molybdenum disilicide was synthesized successfully from element Mo and Si powders using self -propagating high - temperature synthesis technology.
以Mo粉和Si粉为原料,通过自蔓延高温燃烧合成(SHS)的方法成功地制备了MoSi2材料。
2.
Vikers microhardness indentation and single edge notched beam specimen techniques were evaluated, and the modified equation was presented in the measurement of fracture toughness of molybdenum disilicide matrix composites.
对压痕法和单边切口梁法所测MoSi2 基复合材料的断裂韧性作了研究和分析 ,提出了压痕法测量MoSi2 基复合材料断裂韧性的计算修正式。
4) MoSi2 SiC
MoSi2-SiC
1.
The electrical resistivity of the composite MoSi2 SiC containing various SiC contents was calculated by a topological method.
用拓扑法计算了不同显微组织的MoSi2-SiC材料的电阻率,得到的理论推算结果与实验值吻合很好。
5) MoSi2 SiCp
MoSi2-SiCp
6) MoSi_2/Cu
MoSi2/Cu
1.
The results indicate that MoSi_2 is an effective reinforcement for Cu and the MoSi_2/Cu composite exhibit good stability.
结果表明,MoSi2是一种合适的铜基复合材料的增强相,MoSi2/Cu复合材料具有良好的稳定性;MoSi2具有明显的细化晶粒强化基体的作用;随MoSi2含量的增加,MoSi2/Cu复合材料的密度和电导率下降,硬度和抗拉强度表现为先增加后降低;加入2%MoSi2时,复合材料具有最佳的综合性能,其相对密度和电导率分别为97。
补充资料：bioactive glass-ceramic composite reinforced by SiC whisker
分子式：
CAS号：
性质：由碳化硅晶须与生物活性玻璃陶瓷复合而成的生物陶瓷复合材料。高强度、高弹性模量、无毒的碳化硅晶须在陶瓷基材中弥散分布，使材料中的裂纹相对均匀，裂纹扩展发生转向和分支；外力作用下碳化硅晶须拔出时产生的拔出效应，使复合陶瓷的弯曲强度达460MPa，断裂韧性达4.3MPa·m1/2，维伯尔系数高达24.7，标志着它是可承力的生物陶瓷复合材料。
CAS号：
性质：由碳化硅晶须与生物活性玻璃陶瓷复合而成的生物陶瓷复合材料。高强度、高弹性模量、无毒的碳化硅晶须在陶瓷基材中弥散分布，使材料中的裂纹相对均匀，裂纹扩展发生转向和分支；外力作用下碳化硅晶须拔出时产生的拔出效应，使复合陶瓷的弯曲强度达460MPa，断裂韧性达4.3MPa·m1/2，维伯尔系数高达24.7，标志着它是可承力的生物陶瓷复合材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条